Polipropilene compound Omopolimero o Copolimero non caricato, con elevate proprietà meccaniche, sviluppato seguendo le richieste del mercato e gli standard industriali. Prodotti disponibili in un’ampia gamma di colori e in versioni autoestinguenti certificate, alogenate o esente alogeni.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Isoplen® A H F | PP homo, natural colour medium flowability | 12 g/10' | - | 1400 MPa | - | 3,3 Kj/m2 | - | Classe HB | |
| Isoplen® A K F | PP copo, medium flowability | 13 g/10' | - | 1300 MPa | - | 11 Kj/m2 | - | Classe HB | |
| Isoplen® A K Z | PP copo, high flowability | 21 g/10' | - | 1350 MPa | - | 5,6 Kj/m2 | - | Classe HB | |
| Isoplen® FR V2 | PP copo flame retardant low halogen content | 10 g/10' | - | 1400 MPa | - | 10 Kj/m2 | - | Classe V2 YC | |
| Isoplen® H2 T V | PP homo, natural colour, heat stabilized, high flowability | 20 g/10' | - | 1400 MPa | - | 5 Kj/m2 | - | Classe HB | |
| Isoplen® HK X V0 HF | Unfilled. Heat stabilized. Flame Retardant grade without halogens. | 10 g/10' | - | 1600 Mpa | - | 3,5 KJ/m2 | - | Classe V0 YC |
Isoflex®
Polipropilene copolimero, non caricato e non stabilizzato| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Isoflex® C800 | Polypropylene copolymer. | 6 g/10' | - | 800 Mpa | - | 45 KJ/m2 | - | / |
Isodur®
Compounds a base di poliesteri (PBT) in diversi gradi, elevata resistenza a calore e agli agenti chimici e buona stabilità dimensionale. I nostri prodotti possono essere rinforzati fibra di vetro; con ritardanti di fiamma a base di alogeni, listati UL94. I nostri compounds possono essere colorati in base alle specifiche richieste del cliente.| Nome | Compound | Densità ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isodur® 15 10 GF20 V0 | PBT 20% glass fiber reinforced, flame retardant UL94 V0 1,5mm. | 1,57/1,59 g/cm3 | 7000 MPa | 7 Kj/m2 | V0 YC | |
| Isodur® A 15 10 GF20 | PBT 20% glass fiber reinforced. | 1,45 g/cm3 | 5500 MPa | 7 Kj/m2 | HB | |
| Isodur® A 15 10 GF30 | PBT 30% glass fiber reinforced. | 1,56 g/cm3 | 8500 MPa | 8 Kj/m2 | HB |
Isofil®
Polipropilene compound additivato con cariche minerali (T/TC/CaCO3/BaSO4/Mica) standard o ad alte prestazioni, in accordo con le richieste del mercato e gli standard industriali. Prodotti sviluppati per soddisfare il cliente a seconda delle diverse applicazioni, in termini di colori e specifiche tecniche. Disponibili versioni autoestinguenti certificate, alogenate o esente alogeni.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Isofil® H 20 T F UV | 20% talc filled homopolymer polypropylene. UV stabilized. | 15 g/10' | - | 2600 Mpa | - | 2,5 KJ/m2 | - | Classe HB | |
| Isofil® H 20 TP F HS | 20% Talc filled polypropylene homopolymer. Low emission. Compliant to VW44045-PP6.Heat stabilized. | 12 g/10' | - | 2800 Mpa | - | 3 KJ/m2 | - | Classe Hb | |
| Isofil® H 20 TP X | PP homo 20% talc natural colour | 9 g/10' | - | 2600 MPa | - | 3 Kj/m2 | - | Classe HB | |
| Isofil® H 40 C2 F | 40% calcium carbonate filled homopolymer polypropylene. | 13 g/10' | - | 2500 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® H 40 C2 X | 40% calcite filled homopolymer polypropylene. | 9 g/10' | - | 2400 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® H 40 TG S HS | 40% talc filled polypropylene homopolymer. | 10 kg/10' | - | 4100 Mpa | - | 3,5 KJ/m2 | - | Classe HB | |
| Isofil® H 40 TG X HS | 40% talc filled homopolymer polypropylene. Compliant to VW 44045-PP8. Heat stabilized. | 15 g/10' | - | 4000 Mpa | - | 2,5 KJ/m2 | - | Classe HB | |
| Isofil® H 40 TP F | PP homo 40% talc | 12 g/10' | - | 4000 MPa | - | 2,4 Kj/m2 | - | Classe HB | |
| Isofil® HF 2206H L | 10% talc filled polypropylene copolymer. Heat stabilized. Laserable. | 12 g/10' | - | 1500 Mpa | - | 8 KJ/m2 | - | Classe HB | |
| Isofil® HF 6205X | 30% talc filled copolymer polypropylene. UV stabilized. Heat stabilized. | 14 g/10' | - | 2300 Mpa | - | 6 KJ/m2 | - | Classe HB | |
| Isofil® HK 10 TVHM | 10% micro talc filled polypropylene. White colour. | 20 g/10' | - | 2400 MPa | - | 4 Kj/m2 | - | Classe HB YC | |
| Isofil® HK 20 2VH0 | 20% calcium carbonate polypropylene. Heat stabilized. | 16 g/10' | - | 1850 Mpa | - | 2,4 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 20 T V0 | 20% talc filled copolymer polypropylene. Heat stabilized. Flame Retardant grade With halogens | 6 g/10' | - | 2900 Mpa | - | 3,5 KJ/m2 | - | Classe HB | |
| Isofil® HK 20 TCH0 | 20% mineral filled polypropylene. Heast stabilized. | 6 g/10' | - | 2300 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 20 TFH0 | 20% mineral filled polypropylene. Heat stabilized. | 13 g/10' | - | 2300 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 20 TFHH | 20% talc filled polypropylene. Heat stabilized. Detergent Resistant. | 5 g/10' | - | 2200 Mpa | - | 3,9 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 20 TP F HS | 20% talc filled copolymer polypropylene. | 12 g/10' | - | 2200 Mpa | - | 6 KJ/m2 | - | Classe HB | |
| Isofil® HK 25 6VH | 25% talc-calcium carbonate filled polypropylene. | 16 g/10' | - | 2400 Mpa | - | 5 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 25 GVH | 25% talc filled copolymer polypropylene. | 16 g/10' | - | 2200 Mpa | - | 5,1 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 25 GVH1 | 25% talc copolymer polypropylene. Heat stabilized. | 17 g/10' | - | 2000 Mpa | - | 12,9 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 25 TVH0 | 25% talc filled copolymer polypropylene. | 23 g/10' | - | 1800 Mpa | - | 7 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TFH2 | 30% talc filled polypropylene. | 14 g/10' | - | 34600 Mpa | - | 3,8 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TSH1 | 30% talc filled polypropylene homopolymer. Heat stabilized. | 3 g/10' | - | 3500 Mpa | - | 5 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TTH0 | 30% talc polypropylene. | 4 g/10' | - | 3300 Mpa | - | 3,1 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TTH1 | 30% talc filled polypropylene. UV stabilized. Heat stabilized. | 3 g/10' | - | 3400 Mpa | - | 2,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TVH0 | 30% talc filled homopolymer polypropylene. | 20 g/10' | - | 3400 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TVH2 | 30% talc filled polypropylene. | 16 g/10' | - | 3200 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 30 TXH0 | 30% talc filled polypropylene. Heat stabilized. | 8 g/10' | - | 3300 Mpa | - | 2,7 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 35 GVH0 | 35% talc filled copolymer polypropylene. | 21 g/10' | - | 3100 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 40 2FH0 | 40% calcium carbonate filled polypropylene. Heat stabilized. | 13 g/10' | - | 2500 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 40 5FH0 | 40% calcium carbonate polypropylene. | 13 g/10' | - | 2500 Mpa | - | 3,3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 40 TTH0 | 40% talc filled homopolymer polypropylene. Heat stabilized. | 4 g/10' | - | 3800 Mpa | - | 2,4 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 40 TVH0 | 40% talc filled copolymer polypropylene. | 18 g/10' | - | 4000 Mpa | - | 3 KJ/m2 | - | Classe HB YC | |
| Isofil® HK 50 2FH0 | 50% calcium carbonate filled polypropylene. | 20 g/10' | - | 2800 Mpa | - | 3,5 KJ/m2 | - | Classe HB | |
| Isofil® HK 50 C2 V | 50% calcium carbonate homopolymer polypropylene. Heat stabilized. | 18 g/10' | - | 3100 Mpa | - | 2,5 KJ/m2 | - | Classe HB YC | |
| Isofil® HZ 9101D | 40% talc filled homopolymer polypropylene. Good flowability. | 23 g/10' | - | 4100 Mpa | - | 2,5 KJ/m2 | - | Classe HB | |
| Isofil® K 0 T xxx HB | Copolymer polypropylene. | 17 g/10' | - | 1200 Mpa | - | 7,9 KJ/m2 | - | Classe HB YC | |
| Isofil® K 10 T 46.400 AFU | 10% talc filled copolymer polypropylene. Scratch resistant. UV stabilized. | 22 g/10' | - | 1300 Mpa | - | 40 KJ/m2 | - | Classe HB | |
| Isofil® K 10 T 53.180U | 13% talc filled copolymer polypropylene. UV stabilized. Scratch Resistant. | 15 g/10' | - | 1650 Mpa | - | 18 KJ/m2 | - | Classe HB | |
| Isofil® K 20 T 48.450 AFU | 20% talc filled copolymer polypropylene. Impact modified and scratch resistant. UV stabilized. | 19 g/10' | - | 1700 Mpa | - | 45 KJ/m2 | - | Classe HB | |
| Isofil® K 20 T 50.400LCE SR AF | 17% talc filled copolymer polypropylene. Low CLTE and scratch resistant. UV stabilized. | 32 g/10' | - | 1450 Mpa | - | 40 KJ/m2 | - | Classe HB | |
| Isofil® K 20 T xxx HB | 20% talc filled copolymer polypropylene. | 16 g/10' | - | 2300 Mpa | - | 6,5 KJ/m2 | - | Classe HB YC | |
| Isofil® K 20 TP X | PP copo 20% talc | 10 g/10' | - | 2000 MPa | - | 7 Kj/m2 | - | Classe HB | |
| Isofil® K 30 T 50.200LCE SR AF | 30% talc filled copolymer polypropylene. High impact. Scratch resistant. High fluidity. UV stabilized. | 33 g/10' | - | 1700 Mpa | - | 20 KJ/m2 | - | Classe HB | |
| Isofil® K 30 T 60.90L | 30% talc filled copolymer polypropylene. UV stabilized. | 16 g/10' | - | 2300 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isofil® K 40 T | 40% talc filled polypropylene. | 7 g/10' | - | 4200 Mpa | - | 2,6 KJ/m2 | - | Classe HB | |
| Isofil® K 40 T xxx HB | 40% talc filled copolymer polypropylene. Heat stabilized. | 8 g/10' | - | 3800 Mpa | - | 2,6 KJ/m2 | - | Classe HB YC | |
| Isofil® K 40 TP V | PP copo 40% talc | 20 g/10' | - | 3400 MPa | - | 4,2 Kj/m2 | - | Classe HB | |
| Isofil® KGF 4002U | 21,5% talc filled copolymer polypropylene. UV stabilized. | 12 g/10' | - | 2000 Mpa | - | 4 KJ/m2 | - | Classe HB | |
| Isofil® KPZ 4001D | 20% talc filled copolymer polypropylene. Heat stabilized. | 20 g/10' | - | 2400 Mpa | - | 4,7 KJ/m2 | - | Classe HB YC | |
| Isofil® MC 4214Y | 20% talc filled copolymer polypropylene. UV stabilized. Scratch Resistant. | 8 g/10' | - | 2300 Mpa | - | 7 KJ/m2 | - | Classe HB | |
| Isofil® MF 3604Y | 16% talc filled polypropylene. Impact resistance grade. UV stabilized. Scratch Resistant. | 14 g/10' | - | 1500 Mpa | - | 30 KJ/m2 | - | Classe HB | |
| Isofil® MF 4124S | 20% talc filled polypropylene compound. It exhibits high stiffness and low emission properties. Scratch Resistant. | 15 g/10' | - | 2700 Mpa | - | 4 KJ/m2 | - | Classe HB | |
| Isofil® MV 4509Y | 20% talc filled polypropylene copolymer. Impact modified. UV stabilized. Scratch Resistant. | 26 g/10' | - | 1900 Mpa | - | 30 KJ/m2 | - | Classe HB | |
| Isofil® MY 2205Y | 10% talc filled copolymer polypropylene. Low emission grade. Scratch Resistant. | 25 g/10' | - | 1600 Mpa | - | 18 KJ/m2 | - | Classe HB | |
| Isofil® MZ 2102H | 10% talc filled homopolymer polypropylene. Low emission grade. | 25 g/10' | - | 2350 Mpa | - | 3,5 KJ/m2 | - | Classe HB | |
| Isofil® MZ 3506Y | 17% talc filled copolymer polypropylene. Good flowability. Low emission. UV stabilized. Heat stabilized. Scratch Resistant. | 22 g/10' | - | 2000 Mpa | - | 25 KJ/m2 | - | Classe HB | |
| Isofil® PF 4102H | 20% Talc filled polypropylene homopolymer. Low emission. Compliant to VW44045-PP6 and WSS-M4D729-B1. Heat stabilized. | 12 g/10' | - | 2800 Mpa | - | 3 KJ/m2 | - | Classe HB | |
| Isofil® PZ 8103H | 40% talc filled polypropylene homopolymer. Heat stabilized. | 20 g/10' | - | 4300 Mpa | - | 3 KJ/m2 | - | Classe HB | |
| Isofil® RF 3403Y | 15% talc filled polypropylene copolymer. Impact modified. High fluidity. Low CLTE. UV stabilized. Scratch Resistant. | 15 g/10' | - | 1700 Mpa | - | 25 KJ/m2 | - | Classe HB | |
| Isofil® RV 4603S | 20% talc filled impact modified polypropylene. Compliant to TL 52388-F. UV stabilized. Scratch Resistant. | 18 g/10' | - | 2000 Mpa | - | 35 KJ/m2 | - | Classe HB | |
| Isofil® SF 4303U | 20% talc filled copolymer polypropylene with good stiffness and impact resistance. UV stabilized. | 15 g/10' | - | 1800 Mpa | - | 15 KJ/m2 | - | Classe HB | |
| Isofil® SF 4501Y | 20% talc filled copolymer polypropylene. Impact modified grade. UV stabilized. Scratch Resistant. | 14 g/10' | - | 1900 Mpa | - | 20 KJ/m2 | - | Classe HB | |
| Isofil® SV 4118X | 20% talc filled homopolymer polypropylene. Compliant to TL 52658-WD01. UV stabilized. Heat stabilized. | 16 g/10' | - | 2800 Mpa | - | 2,5 KJ/m2 | - | Classe HB | |
| Isofil® SV 4205Y | 20% talc filled polypropylene copolymer. Good flowability and stiffness. UV stabilized. Scratch Resistant. | 16 g/10' | - | 2300 Mpa | - | 6 KJ/m2 | - | Classe HB | |
| Isofil® SW 4909U | 20% talc filled copolymer polypropylene. Impact modified grade with high flowability. UV stabilized. | 40 g/10' | - | 1500 Mpa | - | 40 KJ/m2 | - | Classe HB |
Isoglass®
Polipropilene compound rinforzato con fibre di vetro, legate chimicamente o meccanicamente, con elevate proprietà termiche, di resistenza all’impatto e di rigidità, in accordo con gli standard delle industrie automobilistiche e dell’elettrodomestico. Prodotti disponibili nelle colorazioni e nelle versioni autoestinguenti indicate per i relativi settori, con importanti certificazioni per alogenati e esente alogeni.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Isoglass® 4F 4030U | 22% chemically coupled glass fiber and mineral filled reinforced polypropylene copolymer. Good stiffness and impact strenght balance combined with high flowability. UV stabilized. | 14 g/10' | - | 3200 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® EV 3007U | 15% chemically coupled glass fiber reinforced polypropylene copolymer. High flowability grade and good aesthetical appearance. UV stabilized. | 18 g/10' | - | 2600 Mpa | - | 12 KJ/m2 | - | Classe HB | |
| Isoglass® H 20 CGF X | 20% glass fiber reinforced homopolymer polypropylene. | 8 g/10' | - | 3800 MPa | - | 8 Kj/m2 | - | Classe HB | |
| Isoglass® H 20 CGF X HS | 20% chemically coupled glass fiber reinforced homopolymer polypropylene. Compliant to VW 44045-PP9. Heat stabilized. | 8 g/10' | - | 4000 Mpa | - | 7 KJ/m2 | - | Classe HB | |
| Isoglass® H 20 FVL X | 20% glass fiber polypropylene. Heat stabilized. | 8 g/10' | - | 3900 Mpa | - | 7,4 KJ/m2 | - | Classe HB YC | |
| Isoglass® H 25 CGF C UV | 25% chemically coupled glass fibre reinforced Polypropylene. Antistatic.UV stabilized. | 6 g/10' | - | 5400 Mpa | - | 11 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 CGF 140.80 | 30% glass fiber reinforced homopolymer polypropylene. Compliant to MS-55246 PP140.80. Heat stabilized. | 18 g/10' | - | 5700 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 CGF C | 30% chemically coupled glass fiber reinforced polypropylene. Heat stabilized. | 5 g/10' | - | 6000 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 CGF C UV | 30% chemically coupled glass fiber reinforced polypropylene. Low odor and emission. Compliant to VW44045-PP10 and VW50180. UV stabilized. Heat stabilized. | 5 g/10' | - | 5800 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 CGF F UV | 30% glass fiber reinforced homopolymer polypropylene. UV stabilized. | 13 g/10' | - | 5000 Mpa | - | 8 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 CGF S HS | 30% glass fiber reinforced homopolymer polypropylene. Heat stabilized. | 5 kg/10' | - | 6000 Mpa | - | 10 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 CGF X HS | 30% chemically coupled glass fiber reinforced polypropylene. Heat stabilized. | 8 g/10' | - | 6000 Mpa | - | 10 KJ/m2 | - | Classe HB | |
| Isoglass® H 30 FVL C | PP homo 30% glass fiber. Heat stabilized. | 6 g/10' | - | 5800 MPa | - | 11,5 Kj/m2 | - | Classe HB YC | |
| Isoglass® H 30 FVL V | 30% glass fiber filled homopolymer polypropylene. | 20 g/10' | - | 5700 Mpa | - | 10 KJ/m2 | - | Classe HB YC | |
| Isoglass® H 30 GFT3 C HS | 30% glass fiber and talc filled polypropylene. Compliant to MS-55246 PP130.50. Heat stabilized. | 8 g/10' | - | 4500 Mpa | - | 7 KJ/m2 | - | Classe HB | |
| Isoglass® H 40 CGF C | 40% glass fiber reinforced homopolymer polypropylene. | 7 g/10' | - | 7600 MPa | - | 9 Kj/m2 | - | Classe HB | |
| Isoglass® H3V 6009D | 30% talc filled and glass fiber reinforced polypropylene homopolymer. Heat stabilized. Detergent resistant. | 17 g/10' | - | 4700 Mpa | - | 5 KJ/m2 | - | Classe HB YC | |
| Isoglass® HGV 6002D | 30% glass fiber homopolymer polypropylene. Heat stabilized. Detergent Resistant. | 17 g/10' | - | 5600 Mpa | - | 9,1 KJ/m2 | - | Classe HB YC | |
| Isoglass® HGV 6003X | 30% chemically coupled glass fiber reinforced polypropylene. High flowability. UV stabilized. Chemical Resistant. | 20 g/10' | - | 5500 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® K 20 CGF X | 20% glass fiber reinforced copolymer polypropylene. | 10 g/10' | - | 3400 Mpa | - | 13 KJ/m2 | - | Classe HB | |
| Isoglass® K 30 CGF X | 30% glass fiber reinforced copolymer polypropylene. | 8 g/10' | - | 4000 Mpa | - | 16 KJ/m2 | - | Classe HB | |
| Isoglass® K 40 CGF C | 40% glass fiber reinforced copolymer polypropylene. | 4 g/10' | - | 6200 MPa | - | 15 Kj/m2 | - | Classe HB | |
| Isoglass® SC 6029X | 30% chemically coupled glass fiber reinforced copolymer polypropylene. UV stabilized. Heat stabilized. | 5 g/10' | - | 4500 Mpa | - | 22 KJ/m2 | - | Classe HB | |
| Isoglass® ST 8020N | 40% chemically coupled glass fiber reinforced polypropylene homopolymer. UV stabilized. Heat stabilized. | 4 g/10' | - | 8000 Mpa | - | 10 KJ/m2 | - | Classe HB | |
| Isoglass® SX 4010H | 20% chemically coupled glass fiber reinforced homopolymer polypropylene. Compliant to Renault-Nissan AS8. Heat stabilized. | 10 g/10' | - | 4000 Mpa | - | 8 KJ/m2 | - | Classe HB | |
| Isoglass® SX 4015X | 20% chemically coupled glass fiber reinforced homopolymer polypropylene. Compliant to VW 44045. UV stabilized. Heat stabilized. | 8 g/10' | - | 3800 Mpa | - | 6 KJ/m2 | - | Classe HB | |
| Isoglass® SX 8022H | 40% chemically coupled glass fiber reinforced polypropylene homopolymer. Heat stabilized. | 10 g/10' | - | 7700 Mpa | - | 10 KJ/m2 | - | Classe HB | |
| Isoglass® XX 6014D | 30% chemically coupled glass fiber reinforced polypropylene, high stiffness. Heat stabilized. | 8 g/10' | - | 7000 Mpa | - | 9 KJ/m2 | - | Classe HB |
Isoglass® XT
Polipropilene compound rinforzato con fibre di vetro, legate chimicamente o meccanicamente, con elevate proprietà termiche, di resistenza all’impatto e di rigidità, in accordo con gli standard delle industrie automobilistiche e dell’elettrodomestico. Prodotti disponibili nelle colorazioni e nelle versioni autoestinguenti indicate per i relativi settori, con importanti certificazioni per alogenati e esente alogeni.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Isoglass® XT 1003H | 50% chemically coupled high performance glass fiber reinforced polypropylene homopolymer. High stiffness grade. Heat stabilized. | 3,5 g/10' | - | 13000 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® XT 4001D | 20% chemically coupled glass fiber reinforced polypropylene. | 7 g/10' | - | 4000 Mpa | - | 7 KJ/m2 | - | Classe HB YC | |
| Isoglass® XT 4007U | 20% chemically coupled high performance reinforced polypropylene homopolymer. High stiffness and low emission. Compliant to DBL 5430. UV stabilized. | 7 g/10' | - | 6100 Mpa | - | 9 KJ/m2 | - | Classe HB | |
| Isoglass® XT 6001D | 30% chemically coupled high performance glass fiber reinforced polypropylene compound. | 5 g/10' | - | 6800 Mpa | - | 11 KJ/m2 | - | Classe HB YC | |
| Isoglass® XT 6001H | 30% chemically coupled high performance glass fiber reinforced polypropylene. Heat stabilized. | 3,5 g/10' | - | 6500 Mpa | - | 10 KJ/m2 | - | Classe HB | |
| Isoglass® XT 6010H | 30% chemically coupled high performance glass fiber reinforced polypropylene homopolymer. High stiffness and low emission. | 6 g/10' | - | 8400 Mpa | - | 10 KJ/m2 | - | Classe HB | |
| Isoglass® XT 7001H | 35% chemically coupled glass fiber reinforced polypropylene homopolymer. Low flowability grade. Heat stabilized. | 3 g/10' | - | 8000 Mpa | - | 12 KJ/m2 | - | Classe HB | |
| Isoglass® XT 8008H | 40% chemically coupled high performance glass fiber reinforced polypropylene homopolymer. High stiffness and low emission. | 5 g/10' | - | 10000 Mpa | - | 10 KJ/m2 | - | Classe HB |
Isoglass® LFT
Polipropilene compound rinforzato con fibre di vetro lunghe, ottenuto per pultrusione, che presenta elevate prestazioni termico-meccaniche. Particolarmente indicato in applicazioni strutturali, in cui è possibile sfruttare l’orientazione delle fibre lunghe per incrementare la stabilità dimensionale e la rigidezza del manufatto. Disponibili prodotti con contenuti di fibra in diverse percentuali, anche elevate.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Isoglass® LFT 1001H | PP homo 50% long glass fiber, heat stabilized. | / | - | 10500 MPa | - | 29 Kj/m2 | - | Classe HB | |
| Isoglass® LFT LFT 0603H | 30% chemically coupled long glass fiber reinforced polypropylene compound with very high mechanical properties and heat stabilized. | / | - | 6300 Mpa | - | 21 Kj/m2 | - | Classe HB |
Green Isofil®
Polipropilene compound additivato con cariche minerali contenente percentuali di materiale riciclato post-industriale o post-consumo. I prodotti rispettano gli standard recentemente introdotti dai settori auto ed elettrodomestico.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Green Isofil® HK 40 C F | PP copo 40% calcium carbonate, heat stabilized, detergent resistant. | 20 g/10' | - | 1900 MPa | - | 3,3 Kj/m2 | - | Classe HB | |
| Green Isofil® K 30 T T HS | 30% talc filled polypropylene copolymer. Industrial quality. Heat stabilized. | 3 g/10' | - | 2200 MPa | - | 6 Kj/m2 | - | Classe HB |
Green Isoglass®
Polipropilene compound rinforzato con fibre di vetro contenente percentuali di materiale riciclato post-industriale o post-consumo. I prodotti rispettano gli standard recentemente introdotti dai settori auto ed elettrodomestico.| Nome | Compound | MFR ISO 1133 | MFI (g/10’) ASTM D1238 | MEF ISO 178 | MFI (g/10’) ASTM D1238 | Izod Notched ISO 180/1A | Izod Notched (J/m²) ASTM D256 | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|---|---|---|
| Green Isoglass® H 30 CGF C HS | 30% chemically coupled glass fiber reinforced polypropylene with 30% circular polymer source. Heat stabilized. | 6 g/10' | - | 4900 MPa | - | 9 Kj/m2 | - | Classe HB | |
| Green Isoglass® H 40 CGF X HS | 40% glass fiber reinforced polypropylene. Industrial quality. Heat stabilized. | 10 g/10' | - | 6000 MPa | - | 9 Kj/m2 | - | Classe HB |
Isoblend®
Compounds disponibili in una vasta gamma di leghe polimeriche. Il nostro portfolio comprende gradi rinforzati fibra vetro; formule con ritardanti di fiamma con o senza alogeni, con certificazione UL94. I nostri prodotti possono essere colorati in base alle specifiche richieste del cliente.| Nome | Compound | Densità ISO 1183 | Vicat B/50 ISO 306 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isoblend® A 20 500 V0 | Blend PC/ABS flame retardant UL94 V0 1,5mm, halogen free. | 1,17 g/cm3 | 110 °C | 50 KJ/m2 | V0 YC | |
| Isoblend® A 40 200 V0 | Blend PC/ABS flame retardant UL94 V0 1,5mm, halogen free. | 1,17 g/cm3 | 105 °C | 30 Kj/m2 | V0 YC | |
| Isoblend® A 45 | Blend ABS/PC general purpose, good flow properties. | 1,10 - 1,12 g/cm3 | 110 °C | 30 Kj/m2 | HB | |
| Isoblend® A 45 PG | Blend ABS/PC, suitable for electroplating application. | 1,08 g/cm3 | 110 °C | 45 KJ/m2 | HB | |
| Isoblend® A 50 UV | Blend PC/ABS, UV stabilized. | 1,12 g/cm3 | 120 °C | 50 KJ/m2 | HB | |
| Isoblend® A 65 | Blend PC/ABS general purpose, good flow properties and good impact resistance. | 1,13 - 1,15 g/cm3 | 118 °C | 35 Kj/m2 | HB | |
| Isoblend® A 65 AF UV | Blend PC/ABS, high fluidity, UV stabilized. | 1,12 g/cm3 | 118 °C | 30 KJ/m2 | HB | |
| Isoblend® A 65 PG | Blend PC/ABS, suitable for electroplating application. | 1,11 g/cm3 | 126 °C | 50 KJ/m2 | HB | |
| Isoblend® A 85 | Blend PC/ABS general purpose, good flow properties, good impact and heat resistance. | 1,15 - 1,16 g/cm3 | 129 °C | 55 Kj/m2 | HB | |
| Isoblend® A 85 AF UV | Blend PC/ABS, high fluidity, UV stabilized. | 1,15 g/cm3 | 129 °C | 50 KJ/m2 | HB | |
| Isoblend® A65 GF17 | Blend PC/ABS, 17% glass fiber reinforced. | 1,29 g/cm3 | 127 °C | 10 KJ/m2 | HB | |
| Isoblend® A65 GF20 | Blend PC/ABS 20% glass fiber reinforced. | 1,29 g/cm3 | 130 °C | 9 KJ/m2 | HB | |
| Isoblend® B 65 | Unfilled PC/ABS alloy. Natural colour. | 1,12 g/cm3 | 120 °C | 40 Kj/m2 | HB |
| Nome | Compound | Densità ISO 1183 | MFR ISO 1133 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isoblend® AS 15 15 UV | Blend PC/ASA good UV and weathering resistance, high heat resistance, good impact strength. | 1,13 - 1,16 g/cm3 | 15 gr/10' | 20 Kj/m2 | HB | |
| Isoblend® AS 15 15 V0 UV | Blend PC/ASA flame retardant UL94 V0 3,00mm, UV resistance. | 1,17 g/cm3 | 13 gr/10' | 15 Kj/m2 | V0 |
Isoform®
Compounds di acetalica a base copolimero o omopolimero (POM), con elevata rigidità e con un'eccezionale resistenza all'usura. I nostri prodotti sono disponibili rinforzati con fibra di vetro; modificati all’impatto e lubrificati con silicone, PTFE or bisolfuro di molibdeno. I compounds possono essere colorati in base alle specifiche richieste del cliente.| Nome | Compound | Densità ISO 1183 | MFR ISO 1133 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isoform® A K 03 | POM COP general purpose, high viscosity. | 1,41 g/cm3 | 3 gr/10' | 8 Kj/m2 | HB | |
| Isoform® A K 09 | POM COP general purpose, medium viscosity. | 1,41 g/cm3 | 9 gr/10' | 7 Kj/m2 | HB | |
| Isoform® A K 09 GF25 | POM COP 25% glass fiber. | 1,59 g/cm3 | 4 gr/10' | 6 Kj/m2 | HB | |
| Isoform® A K 09 STZ | POM COP impact modified. | 1,37 g/cm3 | 11 gr/10' | 15 Kj/m2 | HB | |
| Isoform® A K 13 | POM COP general purpose, medium viscosity. | 1,41 g/cm3 | 13 gr/10' | 6 Kj/m2 | HB | |
| Isoform® A K 27 | POM COP general purpose, low viscosity. | 1,41 g/cm3 | 27 gr/10' | 6 Kj/m2 | HB | |
| Isoform® A K 45 | POM COP general purpose, very low viscosity. | 1,41 g/cm3 | 45 gr/10' | 4 Kj/m2 | HB |
Isoryl®
Compounds di Polifenile ossido (PPO), buona resistenza termica, stabilità dimensionale e resistenza all’idrolisi. I prodotti possono essere rinforzati con fibre di vetro e caricato minerale. Disponibili anche in versione a ritardata propagazione di fiamma, esente alogeni e con certificazione UL94. I nostri prodotti possono essere colorati su misura, in base alle specifiche richiese del cliente.| Nome | Compound | Densità ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isoryl® A 120 GF0 V0 | PPO flame retardant UL94 V0 1,5mm. | 1,10 g/cm3 | 2250 MPa | 9 Kj/m2 | V0 YC | |
| Isoryl® A 120 T20 V1 A | PPO 20% mineral filled, flame retartant UL94 V1 1,5mm. | 1,21 g/cm3 | 3600 MPa | 5 Kj/m2 | V1 YC | |
| Isoryl® A 137 | PPO Unfilled. | 1,06 g/cm3 | 2100 MPa | 10 Kj/m2 | HB | |
| Isoryl® A 20 10 GF30 W | PPO 30% glass fiber, WRAS approved. | 1,27 g/cm3 | 6000 MPa | 3 Kj/m2 | HB | |
| Isoryl® A 20 75 GF20 V0 | PPO 20% glass fiber, flame retardant UL94 V0 3,00mm. | 1,24 g/cm3 | 4500 MPa | 3 Kj/m2 | V0 | |
| Isoryl® A 20 90 GF20 W | PPO 20% glass fiber, WRAS approved. | 1,21 g/cm3 | 4500 MPa | 3 Kj/m2 | HB |
Isonyl®
Compounds di poliammide 6 e 66 (PA6 – PA66), con buona resistenza al calore e buone proprietà meccaniche. Il nostro portfolio comprende diversi gradi, rinforzati con fibra di vetro e carbonio o con carica minerale; modificati all’impatto; lubrificati con silicone, PTFE o bisolfuro di molibdeno; a ritardata propagazione di fiamma, con e senza alogeni, listati UL94. I nostri prodotti possono essere colorati su misura, in base alle specifiche richiese del cliente.| Nome | Compound | Densità ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isonyl® 6 GF30 V0 HF | PA6 30% glass fiber, flame retardant UL94 V0 1,5 mm, halogen free. | 1,41 g/cm3 | 9000 MPa | 6 Kj/m2 | V0 YC | |
| Isonyl® A 6 | PA6 general purpose for injection moulding. | 1,13 g/cm3 | 2700 MPa | 4 Kj/m2 | V2 | |
| Isonyl® A 6 GF15 | PA6 15% glass fiber reinforced. | 1,21 g/cm3 | 6000 MPa | 7 Kj/m2 | HB | |
| Isonyl® A 6 GF30 | PA 6 30% glass fiber reinforced. | 1,36 g/cm3 | 8000 Mpa | 12 Kj/m2 | HB | |
| Isonyl® A 6 GF30 HSR | PA6 30% glass fiber reincorced, good impact resistance, heat and hydrolysis resistant. | 1,36 g/cm3 | 8000 Mpa | 12 Kj/m2 | HB | |
| Isonyl® A 6 GF30 ST | PA6 30% glass fiber reinforced, impact modified. | 1,34 g/cm3 | 7300 Mpa | 14 KJ/m2 | HB | |
| Isonyl® A 6 GF30 ST2 | PA6 30% glass fiber reinforced, impact modified. | 1,32 g/cm3 | 6800 Mpa | 17 Kj/m2 | HB | |
| Isonyl® A 6 GF35 | PA6 35% glass fiber reinforced. | 1,38 - 1,41 g/cm3 | 9000 Mpa | 15 KJ/m2 | HB | |
| Isonyl® A 6 GF50 | PA6 50% glass fiber reinforced. | 1,56 g/cm3 | 12000 MPa | 13 Kj/m2 | HB | |
| Isonyl® A 6 GF60 | PA6 60% glass fiber reinforced. | 1,70 g/cm3 | 19000 MPa | 16 Kj/m2 | HB | |
| Isonyl® A 6 GS30 | PA6 30% glass beads reinforced. | 1,34 - 1,36 g/cm3 | 3150 MPa | 3 Kj/m2 | HB | |
| Isonyl® A 6 ST | PA6 impact modified. | 1,13 g/cm3 | 2400 MPa | 8 Kj/m2 | HB | |
| Isonyl® A 6 ST1 | PA6 impact modified. | 1,12 g/cm3 | 2300 MPa | 20 Kj/m2 | HB | |
| Isonyl® A 6 ST2 | PA6 impact modified. | 1,11 g/cm3 | 2000 MPa | 30 Kj/m2 | HB | |
| Isonyl® A 6 STZ | PA6 impact modified. | 1,10 g/cm3 | 1800 MPa | 40 Kj/m2 | HB | |
| Isonyl® A 6 STZX | PA6 high impact modified. | 1,08 g/cm3 | 1600 MPa | 70 Kj/m2 | HB | |
| Isonyl® A 66 | PA66 general purpose for injection moulding. | 1,14 g/cm3 | 2900 MPa | 4 Kj/m2 | V2 | |
| Isonyl® A 66 GF25 V0 | PA66 25% glass fiber, flame retardant UL94 V0 1,5 mm, with halogens. | 1,50/1,55 g/cm3 | 8500 MPa | 9 Kj/m2 | V0 | |
| Isonyl® A 66 GF30 | PA66 30% glass fiber reinforced. | 1,36 g/cm3 | 8500 MPa | 12 Kj/m2 | HB | |
| Isonyl® A 66 GF50 | PA66 50% glass fiber reinforced. | 1,56 g/cm3 | 14000 MPa | 13 Kj/m2 | HB | |
| Isonyl® A 66 ST | PA66 impact modified. | 1,13 g/cm3 | 2500 MPa | 9 Kj/m2 | HB | |
| Isonyl® A 66 ST1 | PA66 impact modified. | 1,12 g/cm3 | 2400 MPa | 20 Kj/m2 | HB | |
| Isonyl® A 66 ST2 | PA66 impact modified. | 1,11 g/cm3 | 2200 MPa | 30 Kj/m2 | HB | |
| Isonyl® A 66 STZ | PA66 impact modified. | 1,10 g/cm3 | 2000 MPa | 40 Kj/m2 | HB | |
| Isonyl® A 66 STZX | PA66 high impact modified. | 1,08 g/cm3 | 1800 MPa | 65 Kj/m2 | HB |
Green Isonyl®
Poliammide 6 rinforzata con fibre di vetro contenente percentuali di materiale riciclato post-industriale o post-consumo. I prodotti rispettano gli standard recentemente introdotti dai settori automotive e utensili tecnici da lavoro in colorazione nera.| Nome | Compound | Densità ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Green Isonyl® I 66 GF25 GW | 25% glass fiber reinforced polyamide 66. Flame retardant grade with GWFI 850°C on 2 mm thickness. Recycled content. | / | 7500 MPa | 7 KJ/m2 | / |
Isoter®
Compound stirenico (ABS-SAN-ASA) disponibile in diversi gradi e in una vasta gamma di fluidità, resistenza all’impatto e al calore, in conformità alle richieste del mercato e agli standard industriali. Alcuni prodotti sono disponibili rinforzati con fibra di vetro; con certificazioni UL94 classe HB o con ritardanti di fiamma a base di alogeni. Il compound può essere colorato, su specifica del cliente e con elevato o basso gloss.| Nome | Compound | Densità ISO 1183 | MFR ISO 1133 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isoter® A 10 100 GF17 | ABS 17% glass fiber reinforced. | 1,18 g/cm3 | 10 gr/10' | 6 Kj/m2 | HB | |
| Isoter® A 10 120 HT | ABS with high heat resistance Vicat B/50 102°C | 1,05 g/cm3 | 10 gr/10' | 12 Kj/m2 | HB | |
| Isoter® A 10 150 HT | ABS with high heat resistance Vicat B/50 105°C. | 1,05 g/cm3 | 10 gr/10' | 12 Kj/m2 | HB | |
| Isoter® A 15 250 AS | ABS medium flow, improved chemical resistance. | 1,04 g/cm3 | 20 gr/10' | 24 Kj/m2 | HB | |
| Isoter® A 20 180 | ABS medium flow, general purposes, good impact resistance. | 1,04 g/cm3 | 20 gr/10' | 17 Kj/m2 | HB | |
| Isoter® A 30 200 FR V0 | ABS flame retardant, UL94 V0 1,5mm. | 1,20 g/cm3 | 30 gr/10' | 20 Kj/m2 | V0 YC | |
| Isoter® A 35 200 | ABS high flow, general purpose, good impact resistance. | 1,04 g/cm3 | 35 gr/10' | 16 Kj/m2 | HB | |
| Isoter® A 5 150 HT LE | ABS very high heat resistance Vicat B/50 108°C, low emission. | 1,05 g/cm3 | 6 gr/10' | 18 Kj/m2 | HB |
Isoclear®
I nostri compound di policarbonato (PC) offrono un’ottima combinazione di tenacità, resistenza all’impatto ed elevata resistenza al calore. I nostri prodotti possono essere rinforzati con fibra vetro, modificati all'impatto e con ritardanti di fiamma, disponibili sia con che senza alogeni, con certificazione UL94. Possono essere colorati su specifica richiesta del cliente, anche in colorazioni trasparenti.| Nome | Compound | Densità ISO 1183 | MFR ISO 1133 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isoclear® A 10 60 | PC medium viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,2 g/cm3 | 10 gr/10' | 60 Kj/m2 | HB | |
| Isoclear® A 10 60 GF0 V0 | PC flame retardant, with halogens, UL94 V0 1,6 mm. | 1,20 g/cm3 | 10 gr/10' | 50 Kj/m2 | V0 YC | |
| Isoclear® A 10 60 GF10 V0 | PC 10% glass fiber reinforced, flame retardant, with halogens, UL94 V0 1,6 mm. | 1,26 - 1,30 g/cm3 | 10 gr/10' | 7 Kj/m2 | V0 YC | |
| Isoclear® A 20 60 | PC low viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,2 g/cm3 | 20 gr/10' | 60 Kj/m2 | HB |
Isostyr®
Compound stirenico (PS) disponibile in diversi gradi, con resistenza all’impatto e al calore secondo gli standard industriali del mercato dell’elettrodomestico ed elettrico. Alcuni prodotti sono disponibili con ritardanti di fiamma a base di alogeni. Il compound può essere colorato su specifica richiesta del cliente.| Nome | Compound | Densità ISO 1183 | MFR ISO 1133 | Izod Notched ISO 180/1A | Infiammabilità UL94 | |
|---|---|---|---|---|---|---|
| Isostyr® A 10 100 V2 | HIPS flame retardant UL94 V2 1,5 mm. | 1,13 g/cm3 | 20 gr/10' | 7 Kj/m2 | V2 | |
| Isostyr® A 10 50 | HIPS medium impact, good heat resistance and high stiffness. | 1,04 g/cm3 | 10 gr/10' | 5 Kj/m2 | HB |