Isodur®
Compound based on different Polyesters and special alloys with wide viscosity range. The products are usually glass fiber reinforced, impact modified, UV stabilized and colored upon specific customer requirement. Availability of flame retardant grades with registered UL certification.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isodur® A 15 10 GF20 | PBT 20% glass fiber reinforced | 1,45 g/cm3 | 5500 MPa | 7 Kj/m2 | Classe HB | Download TDS |
| Isodur® A 15 10 GF30 | PBT 30% glass fiber reinforced | 1,56 g/cm3 | 8500 MPa | 8 Kj/m2 | Classe HB | Download TDS |
| Isodur® A 15 10 GF20 V0 | PBT 20% glass fiber reinforced, flame retardant UL94 V0 1,5mm | 1,57/1,59 g/cm3 | 7000 MPa | 7 Kj/m2 | Classe V0 | Download TDS |
| Isodur® 15 10 GF30 V0 | 30% glass fiber reinforced PBT, flame retardant with halogens. | 1,65 g/cm3 | 9500 Mpa | 8 Kj/m2 | Classe V0 YC | Download TDS |
Isoblend®
Polymer Alloys Compound produced on different base resins combination. The range of products includes glass fiber or carbon fiber reinforcement, UV stabilization and high impact performance; the products may be colored upon specific customer requirement. Halogen based or halogen-free flame retardant with registered UL certification.| Name | Compound | Density ISO 1183 | Vicat B/50 ISO 306 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoblend® A 45 | Blend PC/ABS general purpose, good flow properties | 1,10/1,12 g/cm3 | 110 °C | 30 Kj/m2 | Classe HB | Download TDS |
| Isoblend® A 65 | Blend PC/ABS general purpose, good flow properties and good impact resistance | 1,13/1,15 g/cm3 | 118 °C | 35 Kj/m2 | Classe HB | Download TDS |
| Isoblend® A 85 | Blend PC/ABS general purpose, good flow properties, good impact and heat resistance | 1,15/1,16 g/cm3 | 129 °C | 55 Kj/m2 | Classe HB | Download TDS |
| Isoblend® A 40 200 V0 | Blend PC/ABS flame retardant UL94 V0 1,5mm, halogen free | 1,17 g/cm3 | 105 °C | 50 Kj/m2 | Classe V0 | Download TDS |
| Isoblend® A 65 AF UV | PC/ABS alloy, high fluidity. UV stabilized. | 1,12 g/cm3 | 118 °C | 40 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A 85 AF UV | PC/ABS alloy, high fluidity. UV stabilized. | 1,15 g/cm3 | 129 °C | 50 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A65 GF20 | PC/ABS alloy, 20% glass fiber reinforced. | 1,29 g/cm3 | 130 °C | 9 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A65 GF17 | PC/ABS alloy, 17% glass fiber reinforced. | 1,27 g/cm3 | 127 °C | 7 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A 45 UV | PC/ABS alloy, UV stabilized. | 1,10 – 1,12 g/cm3 | 110 °C | 35 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A 45 PG | PC/ABS alloy. Suitable for electroplating application. | 1,08 g/cm3 | 110 °C | 45 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A 65 PG | PC/ABS alloy. Suitable for electroplating application | 1,11 g/cm3 | 126 °C | 50 KJ/m2 | Classe HB | Download TDS |
| Isoblend® A 20 500 V0 | PC/ABS alloy, Flame retardant, Halogen free | 1,17 g/cm3 | 110 °C | 50 KJ/m2 | Classe V0 | Download TDS |
| Isoblend® A 50 UV | PC/ABS alloy, UV stabilized. | 1,17 g/cm3 | 120 °C | 50 KJ/m2 | Classe HB | Download TDS |
| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoblend® AS 15 15 UV | Blend PC/ASA good UV and weathering resistance, high heat resistance, good impact strength | 1,13/1,16 g/cm3 | 15 gr/10' | 15 Kj/m2 | Classe HB | Download TDS |
| Isoblend® AS 15 15 V0 UV | Blend PC/ASA good UV and weathering resistance, high heat resistance, good impact strength | 1,17 g/cm3 | 13 gr/10' | 50 Kj/m2 | Classe V0 | Download TDS |
Isoform®
Copolymer and Homopolymer acetal resin with a wide melt flow range and impact modified. Glass fiber reinforced, glass beads or mineral filled. Modified with Silicon, PTFE or molybdenum disulfide to improve lubrication. Natural or colored upon specific customer requirement.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoform® A K 03 | POM COP general purpose, high viscosity | 1,41 g/cm3 | 3 gr/10' | 8 Kj/m2 | Classe HB | Download TDS |
| Isoform® A K 09 | POM COP general purpose, medium viscosity | 1,41 g/cm3 | 9 gr/10' | 7 Kj/m2 | Classe HB | Download TDS |
| Isoform® A K 13 | POM COP general purpose, medium viscosity | 1,41 g/cm3 | 13 gr/10' | 6 Kj/m2 | Classe HB | Download TDS |
| Isoform® A K 27 | POM COP general purpose, low viscosity | 1,41 g/cm3 | 27 gr/10' | 6 Kj/m2 | Classe HB | Download TDS |
| Isoform® A K 45 | POM COP general purpose, very low viscosity | 1,41 g/cm3 | 45 gr/10' | 4 Kj/m2 | Classe HB | Download TDS |
| Isoform® A K 09 GF25 | POM COP 25% glass fiber | 1,59 g/cm3 | 4 gr/10' | 6 Kj/m2 | Classe HB | Download TDS |
| Isoform® A K 09 STZ | POM COP impact modified | 1,37 g/cm3 | 11 gr/10' | 15 Kj/m2 | Classe HB | Download TDS |
Isoryl®
Modified Poly-Ethilene-Ether Compound with a wide melt flow range and performing high thermal resistance. The product is normally reinforced with glass fiber and colored upon specific customer requirement. Halogen based or halogen-free flame retardant with registered UL certification.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoryl® A 137 | PPO Unfilled | 1,06 g/cm3 | 2100 MPa | 10 Kj/m2 | Classe HB | Download TDS |
| Isoryl® A 20 90 GF20 W | PPO 20% glass fiber, WRAS approved | 1,21 g/cm3 | 4500 MPa | 8 Kj/m2 | Classe HB | Download TDS |
| Isoryl® A 20 10 GF30 W | PPO 30% glass fiber, WRAS approved | 1,27 g/cm3 | 6000 MPa | 26 Kj/m2 | Classe HB | Download TDS |
| Isoryl® A 20 75 GF20 V0 | PPO 20% glass fiber, flame retardant UL94 V0 3,00mm | 1,24 g/cm3 | 4500 MPa | 25 Kj/m2 | Classe V0 | Download TDS |
| Isoryl® A 120 T20 V1 A | PPO 20% mineral filled, flame retartant UL94 V1 1,5mm | 1,21 g/cm3 | 3600 MPa | 5 Kj/m2 | Classe V1 | Download TDS |
| Isoryl® A 120 GF0 V0 | Unfilled PPO, flame retardant, halogen free. | 1,13 g/cm3 | 2250 MPa | 8 Kj/m2 | Classe V0 YC | Download TDS |
Isonyl®
Polyamide 6 and 66, 66/6 Copolymer, PPA, with heat resistance and impact modified with a wide viscosity range. Glass fiber or carbon fiber reinforced. Glass sphere or mineral filled. Natural and colored upon specific customer requirement. Halogen based or halogen-free flame retardant with registered UL certification.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isonyl® A 6 | PA6 general purpose for injection moulding | 1,13 g/cm3 | 2700 MPa | 4 Kj/m2 | Classe V2 | Download TDS |
| Isonyl® A 6 ST | PA6 impact modified | 1,13 g/cm3 | 2400 MPa | 8 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 ST1 | PA6 impact modified | 1,12 g/cm3 | 2300 MPa | 20 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 ST2 | PA6 impact modified | 1,11 g/cm3 | 2000 MPa | 30 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 STZ | PA6 impact modified | 1,10 g/cm3 | 1800 MPa | 40 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 STZX | PA6 high impact modified | 1,08 g/cm3 | 1600 MPa | 70 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF15 | PA6 15% glass fiber reinforced | 1,21 g/cm3 | 6000 MPa | 7 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF60 | PA6 60% glass fiber reinforced | 1,7 g/cm3 | 19500 MPa | 18 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GS30 | PA6 30% glass beads reinforced | 1,34/1,36 g/cm3 | 3150 MPa | 3 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF30 V0 HF | PA6 30% glass fiber, flame retardant UL94 V0 1,5 mm, halogen free | 1,41 g/cm3 | 9000 MPa | 6 Kj/m2 | Classe V0 | Download TDS |
| Isonyl® A 66 | PA66 general purpose for injection moulding | 1,14 g/cm3 | 2900 MPa | 4 Kj/m2 | Classe V2 | Download TDS |
| Isonyl® A 66 ST | PA66 impact modified | 1,13 g/cm3 | 2500 MPa | 9 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 ST1 | PA66 impact modified | 1,12 g/cm3 | 2400 MPa | 20 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 ST2 | PA66 impact modified | 1,11 g/cm3 | 2200 MPa | 30 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 STZ | PA66 impact modified | 1,10 g/cm3 | 2000 MPa | 40 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 STZX | PA66 high impact modified | 1,08 g/cm3 | 1800 MPa | 65 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 GF30 | PA66 30% glass fiber reinforced | 1,36 g/cm3 | 8500 MPa | 12 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 GF50 | PA66 50% glass fiber reinforced | 1,56 g/cm3 | 14000 MPa | 13 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 66 GF25 V0 | PA66 25% glass fiber, flame retardant, UL94 V0 1,5 mm, with halogens | 1,50/1,55 g/cm3 | 8500 MPa | 9 Kj/m2 | Classe V0 | Download TDS |
| Isonyl® A 6 GF30 | PA 6 30% glass fiber reinforced. | / | 8000 Mpa | 12 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF30 ST2 | PA 6 30% glass fiber reinforced, impact modified. | / | 7500 Mpa | 16 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF50 | PA 6 50% glass fiber reinforced. | / | 12000 Mpa | 13 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF30 HSR | PA 6 30% glass fiber, very good stiffness, good impact resistance, heat and hydrolysis stabilized. | / | 8000 Mpa | 12 Kj/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF35 | 35% glass fiber reinforced Polyamide 6. | / | 9500 Mpa | 15 KJ/m2 | Classe HB | Download TDS |
| Isonyl® A 6 GF30 ST | 30% glass fiber reinforced Polyamide 6, impact modified. | / | 7300 Mpa | 14 KJ/m2 | Classe HB | Download TDS |
Green Isonyl®
Polyamide 6 with Glass Fiber reinforcement formulated with partial use of post-industrial compound and recycled feedstocks. The products are available in accordance with some standards recently introduced by the automotive and tools sectors in black colors.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Green Isonyl® I 66 GF25 GW | 25% glass fiber reinforced polyamide 66. Flame retardant grade with GWFI 850°C on 2 mm thickness. Recycled content. | / | 7500 MPa | 7 KJ/m2 | / | Download TDS |
Isoter®
Styrenic Compound with a wide melt flow rate range, impact modified and heat resistance. The products are available also glass fiber reinforced and colored with matt or high gloss surface, upon specific customer requirement. Halogen based flame retardant. UL certified.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoter® A 20 180 | ABS medium flow, general purposes, good impact resistance | 1,04 g/cm3 | 20 gr/10' | 17 Kj/m2 | Classe HB | Download TDS |
| Isoter® A 35 200 | ABS high flow, general purpose, good impact resistance | 1,04 g/cm3 | 35 gr/10' | 16 Kj/m2 | Classe HB | Download TDS |
| Isoter® A 15 250 AS | ABS medium flow, improved chemical resistance | 1,04 g/cm3 | 20 gr/10' | 22 Kj/m2 | Classe HB | Download TDS |
| Isoter® A 10 120 HT | ABS with high heat resistance Vicat B/50 102°C | 1,05 g/cm3 | 10 gr/10' | 12 Kj/m2 | Classe HB | Download TDS |
| Isoter® A 10 150 HT | ABS with high heat resistance Vicat B/50 105°C | 1,05 g/cm3 | 10 gr/10' | 12 Kj/m2 | Classe HB | Download TDS |
| Isoter® A 5 150 HT LE | ABS very high heat resistance Vicat B/50 108°C, low emission | 1,04 g/cm3 | 6 gr/10' | 18 Kj/m2 | Classe HB | Download TDS |
| Isoter® A 30 200 FR V0 | ABS flame retardant, UL94 V0 1,5mm | 1,04 g/cm3 | 30 gr/10' | 20 Kj/m2 | Classe VO | Download TDS |
| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoter® A 10 100 GF17 | ABS 17% glass fiber reinforced. | 10 gr/10' | 4700 Mpa | 6 Kj/m2 | Classe HB | Download TDS |
Isoclear®
Compound di policarbonato con diverse fluidità. Prodotti rinforzati con fibre di vetro, modificati all’impatto, stabilizzati UV e colorati a seconda delle specifiche richieste del cliente. Disponibili autoestinguenti alogenati o esente alogeni con certificazione UL.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoclear® A 20 60 | PC low viscosity, good mechanical and high heat resistance, for transparent and solid colors | 1,2 g/cm3 | 20 gr/10' | 60 Kj/m2 | Classe HB | Download TDS |
| Isoclear® A 10 60 | PC medium viscosity, good mechanical and high heat resistance, for transparent and solid colors | 1,2 g/cm3 | 10 gr/10' | 60 Kj/m2 | Classe HB | Download TDS |
| Isoclear® A 10 60 GF0 V0 | PC flame retardant, with halogens, UL94 V0 1,6 mm | 1,2 g/cm3 | 10 gr/10' | 60 Kj/m2 | Classe V0 | Download TDS |
| Isoclear® A 10 60 GF10 V0 | PC flame retardant, with halogens, UL94 V0 1,6 mm, 10% glass fiber reinforced | 1,26/1,30 g/cm3 | 10 gr/10' | 7 Kj/m2 | Classe V0 | Download TDS |
Isostyr®
Styrenic Compound, with a wide melt flow rate range, impact modified and heat resistance. Colored upon specific customer requirement. Halogen based flame retardant. UL certified.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isostyr® A 10 50 | HIPS medium impact, good heat resistance and high stiffness | 1,04 g/cm3 | 10 gr/10' | 5 Kj/m2 | Classe HB | Download TDS |
| Isostyr® A 10 100 V2 | HIPS flame retardant UL94 V2 1,5 mm | 1,13 g/cm3 | 20 gr/10' | 7 Kj/m2 | Classe V2 | Download TDS |
Dafneloy® V
Compound based on different Polyesters and special alloys with wide viscosity range. The products are usually glass fiber reinforced, impact modified, UV stabilized and colored upon specific customer requirement. Availability of flame retardant grades with registered UL certification.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneloy® V VB P03 | PBT 15% glass fiber, high gloss for aestetic parts | 1,41/1,44 g/cm3 | 4500 MPa | 3 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® V VB P06 | PBT 30% glass fiber reinforced | 1,56 g/cm3 | 8500 MPa | 8 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® V VXA P06 | PBT 30% glass fiber reinforced, flame retardant UL94 V0 1,7mm | 1,65 g/cm3 | 9500 MPa | 8 Kj/m2 | Classe V0 | Download TDS |
Dafneloy® D
Acrylic Thermoplastic Compound with a wide viscosity range and impact modified. Product available on transparent colored upon specific customer requirement.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneloy® D DA8 | PMMA medium flow, high mechanical strength, for transparent and solid colors | 1,16/1,18 g/cm3 | 7 gr/10' | 2 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® D DA9 | PMMA low flow, high mechanical strength, for transparent and solid colors | 1,16/1,18 g/cm3 | 3 gr/10' | 2 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® D DH | PMMA good impact resistance | 1,16 g/cm3 | 1,5 gr/10' | 6 Kj/m2 | Classe HB | Download TDS |
Dafneblend®
Polymer Alloys Compound produced on different base resins combination. The range of products includes glass fiber or carbon fiber reinforcement, UV stabilization and high impact performance; the products may be colored upon specific customer requirement. Halogen based or halogen-free flame retardant with registered UL certification.| Name | Compound | Density ISO 1183 | Vicat B/50 ISO 306 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneblend® PM 200 | Blend PC/ABS general purpose, good flow properties | 1,10/1,12 g/cm3 | 110 °C | 30 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PM 500 | Blend PC/ABS general purpose, good flow properties and good impact resistance | 1,13/1,15 g/cm3 | 118 °C | 35 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PM 700 | Blend PC/ABS general purpose, good flow properties, good impact and heat resistance | 1,15/1,16 g/cm3 | 129 °C | 55 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PM 750XF | Blend PC/ABS flame retardant UL94 V0 1,5mm, halogen free, ball pressure test 125°C | 1,16 g/cm3 | 130 °C | 50 Kj/m2 | Classe V0 | Download TDS |
| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneblend® PM 700XF | Blend PC/ABS flame retardant UL94 V0 1,5 mm, halogen free | 1,18 g/cm3 | 2300 MPa | 40 Kj/m2 | Classe V0 YC | Download TDS |
| Dafneblend® PL 200/E | Blend PC/ABS general purpose, good flow properties | 1,22 g/cm3 | 2200 MPa | 50 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PL 300/EC | Blend PC/ABS general purpose, good flow properties and good impact resistance | 1,18 g/cm3 | 1600 MPa | 60 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PL 706 | Blend PC/ABS general purpose, good flow properties, good impact and heat resistance | 1,47/1,49 g/cm3 | 8000 MPa | 10 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PM700/B | PC/ABS alloy. Easy flow grade, good mechanical and thermal characteristics. Antistatic. UV stabilized | 1,15 – 1,16 g/cm3 | 2500 Mpa | 50 Kj/m2 | Classe HB | Download TDS |
| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneblend® PK 201 | Blend PA/ABS good mechanical properties, good chemical resistance | 1,07 g/cm3 | 30 gr/10' | 60 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PK 202 | Blend PA/ABS high flowability and good mechanical properties, good chemical resistance | 1,06 g/cm3 | 55 gr/10' | 50 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PX 200 L | Blend PC/ASA good UV and weathering resistance, good impact strength | 1,10/1,13 g/cm3 | 12 gr/10' | 40 Kj/m2 | Classe HB | Download TDS |
| Dafneblend® PX500 L | PC/ASA alloy very high heat resistance, good impact strength, good toughness and low warpage. Good resistance to weathering. | 1,13 – 1,16 g/cm3 | 15 g/10' | 40 Kj/m2 | Classe HB | Download TDS |
Dafnelan®
Copolymer and Homopolymer acetal resin with a wide melt flow range and impact modified. Glass fiber reinforced, glass beads or mineral filled. Modified with Silicon, PTFE or molybdenum disulfide to improve lubrication. Natural or colored upon specific customer requirement.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnelan® LR2 | POM OMO general purpose, high viscosity | 1,42 g/cm3 | 2 gr/10' | 15 Kj/m2 | Classe HB | Download TDS |
| Dafnelan® LR12 | POM OMO general purpose, medium viscosity | 1,4 g/cm3 | 12 gr/10' | 9 Kj/m2 | Classe HB | Download TDS |
| Dafnelan® LR9 P03/E | POM OMO medium viscosity, 15% glass fiber, high stiffness, low warpage | 1,5 g/cm3 | 8 gr/10' | 5 Kj/m2 | Classe HB | Download TDS |
| Dafnelan® GR9 T02 | POM COP PTFE modified | 1,45 g/cm3 | 9 gr/10' | 5 Kj/m2 | Classe HB | Download TDS |
| Dafnelan® GR9 T04 | POM COP PTFE modified | 1,48/1,50 g/cm3 | 9 gr/10' | 5 Kj/m2 | Classe HB | Download TDS |
| Dafnelan® GR9 MS1 | POM COP lubricated MoS2 | 1,4 g/cm3 | 10 gr/10' | 6 Kj/m2 | Classe HB | Download TDS |
Dafnetec®
High Performance Engineering Compound with a wide range of properties. Glass fiber or carbon fiber reinforced with improved impact resistance. Natural and colored upon specific customer requirement.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnetec® PPS P08 | PPS 40% glass fiber, flame retardante UL94 V0 1,6mm | 1,66/1,68 g/cm3 | 15200 MPa | 10 Kj/m2 | Classe V0 | Download TDS |
| Dafnetec® PPS G12 | PPS glass fiber and mineral filler, flame retardante UL94 V0 1,6mm | 1,96/1,98 g/cm3 | 17500 MPa | 11 Kj/m2 | Classe V0 | Download TDS |
Dafnetherm®
Thermal conductive compound based on different resins available in a wide products range.| Name | Compound | Surface Resistivity IEC 93 | Thermal conductivity ISO 22007-2 - In-Plane | Thermal conductivity ISO 22007-2 - Through-Plane | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnetherm® PPGR16 | Crystalline carbon additive, thermal conductive, electrical conductive | 1E03 Ohm | 10 W/mK | 3 W/mK | Classe HB | Download TDS |
| Dafnetherm® PPBN16 | Inorganic filler, thermal conductive, electrical insulating | > 1E12 Ohm | 9 W/mK | 1,4 W/mK | Classe HB | Download TDS |
Dafneohm®
Electrical conductive compound based on different resins available in a wide products range.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Surface Resistivity IEC 60093 | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneohm® 6A KP06 | PA6 reinforced, electrically conductive | 1,32/1,34 g/cm3 | 14000 MPa | 5E03 Ohm | Classe HB | Download TDS |
| Dafneohm® EC CB 4 | PP electrically conductive | 1,02 g/cm3 | 1000 MPa | 3E04 Ohm | Classe HB | Download TDS |
| Dafneohm® EH K22_D | PP reinforced, electrically conductive | 1 g/cm3 | 8000 MPa | 1E02 Ohm | Classe HB | Download TDS |
Dafnemid®
Polyamide 6 and 66, 66/6 Copolymer, PPA, with heat resistance and impact modified with a wide viscosity range. Glass fiber or carbon fiber reinforced. Glass sphere or mineral filled. Natural and colored upon specific customer requirement. Halogen based or halogen-free flame retardant with registered UL certification.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnemid® 6A P06 | PA6 30% glass fiber reinforced | 1,36 g/cm3 | 8000 MPa | 12 Kj/m2 | Classe HB | Download TDS |
| Dafnemid® 6A MS1 | PA6 lubricated with MoS2 | 1,14 g/cm3 | 2600 MPa | 5 Kj/m2 | Classe HB | Download TDS |
| Dafnemid® 6XA P04 | PA6 20% glass fiber, flame retardant UL94 V0 1,7 mm, with halogen | 1,54 g/cm3 | 6800 MPa | 6 Kj/m2 | Classe V0 GWFI 960, GWIT 850 | Download TDS |
| Dafnemid® 66A K04 | PA66 20% carbon fiber | 1,22 g/cm3 | 12000 MPa | 5 Kj/m2 | Classe HB | Download TDS |
| Dafnemid® 66A MS1 | PA66 lubricated MoS2 | 1,10/1,12 g/cm3 | 2000 MPa | 7 Kj/m2 | Classe HB | Download TDS |
| Dafnemid® 66A T04 | PA66 lubricated Teflon | 1,26 g/cm3 | 2800 MPa | 4 Kj/m2 | Classe HB | Download TDS |
| Dafnemid® 66XA P05/T | PA66 25% glass fiber, heat stabilized, flame ritardant UL94 V0 0,8 mm, with halogens | 1,50/1,55 g/cm3 | 8500 MPa | 9 Kj/m2 | Classe V0 | Download TDS |
| Dafnemid® 6A | Unfilled. Medium viscosity. | 1,13 g/cm3 | 2700 MPa | 4 Kj/m2 | Classe V2 | Download TDS |
| Dafnemid® 6A P12/T | 60% glass fiber. Very high rigidity and strenght.Heat stabilized. | 1,70 g/cm3 | 18000 MPa | 16 Kj/m2 | Classe HB | Download TDS |
Dafneloy® M
Polycarbonate Compound with a wide MFI range. The products may be glass fiber reinforced, impact modified, UV stabilized and colored upon specific customer requirement. Halogen based or halogen-free flame retardant. Registered UL certification available.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneloy® M A | PC low viscosity, good mechanical and high heat resistance, for transparent and solid colors | 1,2 g/cm3 | 20 gr/10' | 55 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® M B | PC medium viscosity, good mechanical and high heat resistance, for transparent and solid colors | 1,2 g/cm3 | 12 gr/10' | 65 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® M C | PC high viscosity, good mechanical and high heat resistance, for transparent and solid colors | 1,2 g/cm3 | 8 gr/10' | 70 Kj/m2 | Classe HB | Download TDS |
| Dafneloy® M XF | PC flame retardant, halogen free, UL94 V0 1,6 mm | 1,2 g/cm3 | 10 gr/10' | 60 Kj/m2 | Classe V0 | Download TDS |
| Dafneloy® M XF EA | PC flame retardant, halogen free, UL94 V0 1,0 mm, impact modified | 1,18 g/cm3 | 8 gr/10' | 70 Kj/m2 | Classe V0 | Download TDS |
| Dafneloy® M XA P02 | PC flame retardant, with halogens, UL94 V0 1,6 mm, 10% glass fiber reinforced | 1,26/1,30 g/cm3 | 10 gr/10' | 10 Kj/m2 | Classe V0 | Download TDS |
| Dafneloy® M MXF P02 | PC flame retardant, halogen free, UL94 V0 1,6 mm, 10% glass fiber reinforced | 1,26/1,30 g/cm3 | 10 gr/10' | 7 Kj/m2 | Classe V0 | Download TDS |
| Dafneloy® M MA/L | PC unfilled, low viscosity, good mechanical characteristics and high heat resistance. UV stabilized. | 1,20 g/cm3 | 20 gr/10' | 55 Kj/m2 | Classe HB | Download TDS |
Dafnelac®
Styrenic Compound with a wide melt flow rate range, impact modified and heat resistance. The products are available also glass fiber reinforced and colored with matt or high gloss surface, upon specific customer requirement. Halogen based flame retardant. UL certified.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnelac® KE | ABS low flow, high impact resistance, suitable for extrusion and vacuumforming | 1,04 g/cm3 | 5 gr/10' | 25 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® SN | ABS medium flow, general purposes, good impact resistance | 1,04 g/cm3 | 26 gr/10' | 17 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® SF | ABS high flow, general purpose, good impact resistance | 1,04 g/cm3 | 35 gr/10' | 16 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® SN AC | ABS medium flow, improved chemical resistance | 1,04 g/cm3 | 22 gr/10' | 22 Kj/m2 | Classe HB YC | Download TDS |
| Dafnelac® TM | ABS medium heat resistance Vicat B/50 100°C | 1,05 g/cm3 | 20 gr/10' | 12 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® TH | ABS high heat resistance Vicat B/50 102°C | 1,05 g/cm3 | 13 gr/10' | 12 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® TX | ABS very high heat resistance Vicat B/50 110°C | 1,05 g/cm3 | 6 gr/10' | 11 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® FXC | ABS flame retardant, UL94 V0 - 5VA on 1,7mm | 1,18/1,20 g/cm3 | 25 gr/10' | 10 Kj/m2 | Classe VO - 5VA YC | Download TDS |
| Dafnelac® FXC T | ABS flame retardant, with improved heat resistant, UL94 V0 - 5VA on 1,7mm | 1,2 g/cm3 | 25 gr/10' | 10 Kj/m2 | Classe VO - 5VA | Download TDS |
| Dafnelac® AS3/LT | ASA improved thermal resistance, good chemical, UV and weathering resistance | 1,07 g/cm3 | 10 gr/10' | 12 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® NRP | SAN general purpose for injection moulding, for transparent and solid colors | 1,07 g/cm3 | 15 gr/10' | 2 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® NRP P04 | SAN 20% glass fiber reinforced | 1,22 g/cm3 | 9 gr/10' | 3 Kj/m2 | Classe HB | Download TDS |
| Dafnelac® SF/B ATX | Easy flow and good mechanical properties.Antistatic.UV stabilized. | 1,04 g/cm3 | 35 gr/10' | 15 KJ/m2 | HB YC | Download TDS |
| Dafnelac® SF/B | ABS high flow, general purpose. UV stabilized. | 1,04 g/cm3 | 35 gr/10' | 16 KJ/m2 | HB YC | Download TDS |
| Dafnelac® SF/A | High flow ABS. Antistatic. | 1,04 g/cm3 | 35 gr/10' | 16 KJ/m2 | HB YC | Download TDS |
| Dafnelac® AS2B | ASA high flow, good mechanical properties. Antistatic. UV stabilized. | 1,07 g/cm3 | 30 gr/10' | 10 KJ/m2 | HB YC | Download TDS |
| Dafnelac® FXC B | ABS. Good mechanical properties. No blooming product. Antistatic. UV stabilized. Flame Retardant grade With halogens. | 1,18/1,20 g/cm3 | 40 gr/10' | 11 KJ/m2 | V0 - 5VA YC | Download TDS |
| Dafnelac® AS2L | Good mechanical propertis, UV stabilized. | 1,07 g/cm3 | 5 gr/10' | 10 KJ/m2 | Classe HB YC | Download TDS |
Dafnestil®
Styrenic Compound, with a wide melt flow rate range, impact modified and heat resistance. Colored upon specific customer requirement. Halogen based flame retardant. UL certified.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnestil® KU | GPPS good fluidity and good heat resistance | 1,05 g/cm3 | 10 gr/10' | 1,7 Kj/m2 | Classe HB | Download TDS |
| Dafnestil® AM | HIPS medium impact, good heat resistance and high stiffness | 1,04 g/cm3 | 10 gr/10' | 5 Kj/m2 | Classe HB | Download TDS |
| Dafnestil® AT | HIPS high impact, heat resistant and high stiffness | 1,04 g/cm3 | 5 gr/10' | 6 Kj/m2 | Classe HB | Download TDS |
| Dafnestil® AXR | HIPS high impact, flame retardant UL94 V0 1,6mm - GWFI 960 2,00mm | 1,14/1,18 g/cm3 | 10 gr/10' | 6 Kj/m2 | Classe V0 - GWFI 960 | Download TDS |
| Dafnestil® AXB | HIPS high impact, flame retardant UL94 V2 1,6mm - GWFI 850 1,00mm | 1,10/1,12 g/cm3 | 12 gr/10' | 6 Kj/m2 | Classe V2 - GWFI 850 | Download TDS |
| Dafnestil® AXE | HIPS high impact, flame retardant UL94 V2 - GWFI 960 1,00mm | 1,17 g/cm3 | 6 gr/10' | 5 Kj/m2 | Classe V2 - GWFI 960 | Download TDS |
| Dafnestil® AXF | HIPS high impact, flame retardant UL94 V2 - GWFI 750 1,00mm | 1,14/1,17 g/cm3 | 7 gr/10' | 5 Kj/m2 | Classe V2 - GWFI 750 | Download TDS |