BioComp®
BioComp® is an innovative bioplastic product family which contain high renewable content. BioComp® is a fully biodegradable and compostable family’s compound which offer excellent mechanical properties. Developed for blow film, sheet extrusion/thermoforming and injection molding application. Can be easily processed in conventional extrusion line and injection molding machines.| Name | MFI ISO 1133 | Tensile stress at break MD ISO 527-3 | Tensile elong. at break MD ISO 527-3 | Ok Compost Industrial | Ok Compost Home | European Bioplastic Seedling | BPI Compostable | DIN Certco Home | DIN Certco Industrial | CSI High Perf. Biopolymer | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| BioComp® BF 01HP | 2,5 | 20 | 450 |  |  |  |  |  |  | - | |
| BioComp® BF 6535 BB | 1,0-3,0 | 17-18 | 400-500 | | | - | - | - | - | - | |
| BioComp® BF 7210 | 3,0-5,0 | 22-23 | 270-360 | | - | | | - | | - | |
| BioComp® BF 7210 (EE) | 2,0 | 20 | 270 | | - | - | - | - | - | - | |
| BioComp® BF 7210S | 3,0-4,5 | 15-19 | 455 | | - | | | | |  | |
| BioComp® BF 8515 | 3,5-5,5 | 20-28 | 150-300 | | - | - | - | - | - | - | |
| BioComp® PAPER03 | 4,0 | 20 | 2 | | - | - | - | - | - | - | |
| BioComp® CF04 | 1,5 | 65 | 3 | | - | - | - | - | - | - | |
| BioComp® FLEX RAW05 | 5,5 | 30 | 550 | | | - | - | - | - | - |
| Name | Density ISO 1183 | Calcium Carbonate Content Calcium (%) | Ok Compost Industrial | Ok Compost Home | |
|---|---|---|---|---|---|
| BioComp® Microfiller XP-Bio | 1,9 | 70 | | - |
| Name | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | HDT ISO 75-1 | Ok Compost Industrial | |
|---|---|---|---|---|---|---|
| BioComp® IM 2368 | 25 | 7500 | 3 | 50 | | |
| BioComp® IM 95 | 34 | 6960 | 2,7 | 59 | | |
| BioComp® IM 95CP | 10 | 1900 | 3 | 95 | | |
| BioComp® IM 95HD | 22 | 4040 | 3 | 95 | | |
| BioComp® IM CFLEX | 5 | 3260 | 2,7 | 87 | |
Sertene® PP
Recycled Polypropylene Homopolymer and Copolymer for injection moulding, extrusion and thermoforming.| Name | Polymer | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | |
|---|---|---|---|---|---|
| Sertene® PP C200R RC | Polypropylene in pellet form | 0,92 g/cm3 | 7,0 g/10' | 5,5 kJ/m2 | |
| Sertene® PP X200C BK | Polypropylene in pellet form | 0,92 g/cm3 | 10 g/10' | 5,5 kJ/m2 | |
| Sertene® PP X200C LG | Polypropylene in pellet form | 0,92 g/cm3 | 10 g/10' | 5 kJ/m2 | |
| Sertene® PP X200C RC | Polypropylene in pellet form | 0,92 g/cm3 | 10 g/10' | 5,5 kJ/m2 |
Xelter® T
Unsaturated SBC based TPE’s. Overmolding and Coextrusion onto PP and PP compounds. Custom developed grades for technical applications.| Name | Type | Hardness Shore A ISO 868 | Density ISO 1183 1/A | |
|---|---|---|---|---|
| Xelter® T 310/320A70-XXX-YYY | TPS-(SBS) | 70 3s | 0,95 g/cm3 | |
| Xelter® T 311/321A40-XXX-YYY | TPS-(SBS) | 40 3s | 1,00 g/cm3 | |
| Xelter® T 311/321A45-XXX-YYY-F2 | TPS-(SBS) | 45 3s | 1,00 g/cm3 | |
| Xelter® T 311/321A50-XXX-YYY-F2 | TPS-(SBS) | 50 3s | 1,00 g/cm3 | |
| Xelter® T 311/321A70-XXX-YYY-F | TPS-(SBS) | 70 3s | 1,00 g/cm3 | |
| Xelter® T 311/321A75-XXX-YYY-F | TPS-(SBS) | 75 3s | 1,00 g/cm3 | |
| Xelter® T 312/322A40-XXX-YYY | TPS-(SBS) | 40 3s | 1,10 g/cm3 | |
| Xelter® T 312/322A45-XXX-YYY | TPS-(SBS) | 45 3s | 1,10 g/cm3 | |
| Xelter® T 312/322A60-XXX-YYY | TPS-(SBS) | 60 3s | 1,10 g/cm3 | |
| Xelter® T 313/323A75-XXX-YYY | TPS-(SBS) | 75 3s | 1,20 g/cm3 |
Dafnelen®
Homopolymer and Copolymer Polypropylene Compound with high mechanical properties, developed in accordance with market demands and industry standards. Products available in a wide range of colors and certified flame retardant versions available both halogenated and halogen-free.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnelen® HP 605/SW | PP homo 30% glass fiber, flame retardant V0 | 4 g/10' | 8000 MPa | 7 Kj/m2 | Classe V0 YC | |
| Dafnelen® HP 505/SW | PP homo 25% glass fiber, flame retardant V0 | 5 g/10' | 6500 MPa | 6 Kj/m2 | Classe V0 | |
| Dafnelen® CR 09/K | PP copo flame retardant halogen free UL94 V0 (0,8mm) | 10 g/10' | 1900 MPa | 3,5 Kj/m2 | Classe V0-5VA YC | |
| Dafnelen® HP 1003/S | 50% glass fibers chemical grafting. | 3 g/10' | 10500 Mpa | 12 KJ/m2 | Classe HB | |
| Dafnelen® HR 17/Y | Unfilled homopolymer polypropylene.Flame Retardant grade Halogen-free according to IEC 61249-2-21 | 17 g/10' | 1500 Mpa | 5 KJ/m2 | Classe V2 |
Sertene® PE
Recycled Polyethylene High Density for extrusion and blow-molding.| Name | Polymer | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | |
|---|---|---|---|---|---|
| Sertene® PE HDGVE 1100 | Polyethylene in pellet form | 0,96 g/cm3 | 1,5 g/10' | 11,5 kJ/m2 | |
| Sertene® PE HDBIA 0300 | Polyethylene in pellet form | 0,96 g/cm3 | 1,75 g/10' | 15 kJ/m2 | |
| Sertene® PE HDGRI 0201 | Polyethylene in pellet form | 1,00 g/cm3 | 1,55 g/10' | 10 kJ/m2 | |
| Sertene® PE HDGRI 0410 | Polyethylene in pellet form | 0,96 g/cm3 | 1,75 g/10' | 15 kJ/m2 | |
| Sertene® PE HDNER 0211 | Polyethylene in pellet form | 0,96 g/cm3 | 1,6 g/10' | 11 kJ/m2 | |
| Sertene® PE HDNER 1100 | Polyethylene in pellet form | 0,96 g/cm3 | 1,6 g/10' | 12 kJ/m2 | |
| Sertene® PE HDNER 1101 | Polyethylene in pellet form | 0,96 g/cm3 | 1,7 g/10' | - | |
| Sertene® PE HDROS 0200 | Polyethylene in pellet form | 0,96 g/cm3 | 1,4 g/10' | 13 kJ/m2 | |
| Sertene® PE HDVER 0200 | Polyethylene in pellet form | 0,96 g/cm3 | 1,5 g/10' | 12 kJ/m2 |
Xelter® S
Saturated SBC based TPE’s for Injection Molding and Extrusion. Overmolding and Coextrusion onto PP and PP compounds. All hardnesses from 0 to 90 Sh A. Different densities from 0.9 to 1.3gr/cm2. Flame retardant grades. Food and drink water contact grades. Mass colored grades. Custom developed grades.| Name | Type | Hardness Shore A ISO 868 | Density ISO 1183 1/A | |
|---|---|---|---|---|
| Xelter® S 110A60 B01 EG0 F | TPS-(SEBS/SEPS) | 58 3s | 0,90 g/cm3 | |
| Xelter® S 110/120A10-XXX-YYY | TPS-(SEBS/SEPS) | 10 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A20-XXX-YYY | TPS-(SEBS/SEPS) | 20 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A30-XXX-YYY | TPS-(SEBS/SEPS) | 30 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A40-XXX-YYY | TPS-(SEBS/SEPS) | 40 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A40-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 40 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A50-XXX-YYY | TPS-(SEBS/SEPS) | 50 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A50-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 50 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A55-XXX-YYY-G1 | TPS-(SEBS/SEPS) | 55 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A55-XXX-YYY-G2 | TPS-(SEBS/SEPS) | 55 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A60-XXX-YYY | TPS-(SEBS/SEPS) | 60 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A60-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 60 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A60-XXX-YYY-G2 | TPS-(SEBS/SEPS) | 60 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A70-XXX-YYY | TPS-(SEBS/SEPS) | 70 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A70-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 70 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A80-XXX-YYY | TPS-(SEBS/SEPS) | 80 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A80-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 80 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A90-XXX-YYY | TPS-(SEBS/SEPS) | 90 3s | 0,88 g/cm3 | |
| Xelter® S 110/120A90-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 90 3s | 0,88 g/cm3 | |
| Xelter® S 111/121A20-XXX-YYY | TPS-(SEBS/SEPS) | 20 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A30-XXX-YYY | TPS-(SEBS/SEPS) | 30 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A40-XXX-YYY | TPS-(SEBS/SEPS) | 40 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A50-XXX-YYY | TPS-(SEBS/SEPS) | 50 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A50-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 50 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A60-XXX-YYY | TPS-(SEBS/SEPS) | 60 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A60-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 60 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A70-XXX-YYY | TPS-(SEBS/SEPS) | 70 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A70-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 70 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A80-XXX-YYY | TPS-(SEBS/SEPS) | 80 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A80-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 80 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A90-XXX-YYY | TPS-(SEBS/SEPS) | 90 3s | 1,00 g/cm3 | |
| Xelter® S 111/121A90-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 90 3s | 1,00 g/cm3 | |
| Xelter® S 112/122A30-XXX-YYY | TPS-(SEBS/SEPS) | 30 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A40-XXX-YYY | TPS-(SEBS/SEPS) | 40 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A50-XXX-YYY | TPS-(SEBS/SEPS) | 50 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A50-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 50 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A60-XXX-YYY | TPS-(SEBS/SEPS) | 60 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A60-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 60 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A70-XXX-YYY | TPS-(SEBS/SEPS) | 70 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A70-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 70 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A80-XXX-YYY | TPS-(SEBS/SEPS) | 80 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A80-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 80 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A90-XXX-YYY | TPS-(SEBS/SEPS) | 90 3s | 1,10 g/cm3 | |
| Xelter® S 112/122A90-XXX-YYY-E1 | TPS-(SEBS/SEPS) | 90 3s | 1,10 g/cm3 | |
| Xelter® S 113/123A30-XXX-YYY | TPS-(SEBS/SEPS) | 30 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A40-XXX-YYY | TPS-(SEBS/SEPS) | 40 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A40-XXX-YYY-G1 | TPS-(SEBS/SEPS) | 40 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A45-XXX-YYY-G1 | TPS-(SEBS/SEPS) | 45 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A50-XXX-YYY | TPS-(SEBS/SEPS) | 50 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A60-XXX-YYY | TPS-(SEBS/SEPS) | 60 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A70-XXX-YYY | TPS-(SEBS/SEPS) | 70 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A80-XXX-YYY | TPS-(SEBS/SEPS) | 80 3s | 1,20 g/cm3 | |
| Xelter® S 113/123A90-XXX-YYY | TPS-(SEBS/SEPS) | 90 3s | 1,20 g/cm3 |
Dafneglass®
Polypropylene Reinforced with Glass Fiber, chemically coupled or mechanical, with high thermal, impact and stiffness properties, aligned with the standards of the automotive and household appliance industries.The products are available in the color range and flame retardant grades indicated by the sectors with relevant certifications both halogenated and halogen-free.
| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneglass® HP 505/K | PP homo 25% glass fiber, flame retardant grade without halogens, heat stabilized. | 3,5 g/10' | 7000 MPa | 7,3 Kj/m2 | Classe V0 | |
| Dafneglass® HP 605/K | 30% chemically coupled glass fiber reinforced polypropylene. V0 flame retardant grade. Heat stabilized. Flame Retardant grade Without halogens. | 2 g/10' | 7600 Mpa | 8 KJ/m2 | Classe HB |
Dafneloy® V
Polyesters compounds (PBT) available in different grades, high heat and chemical resistant, good dimension stability. Our products can be glass fiber reinforced; halogen-based flame retardant, UL94 certified. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneloy® V B P03 | PBT 15% glass fiber. | 1,41 - 1,44 g/cm3 | 4500 MPa | 3 Kj/m2 | HB | |
| Dafneloy® V B P06 | PBT 30% glass fiber reinforced. | 1,56 g/cm3 | 8500 MPa | 8 Kj/m2 | HB | |
| Dafneloy® V XA P06 | PBT 30% glass fiber, flame retardant UL94 V0 1,7mm. | 1,65 g/cm3 | 9500 MPa | 8 Kj/m2 | V0 YC |
Dafneloy® D
Acrylic Thermoplastic compounds (PMMA) with high transparency and gloss. Our products are available listed UL94, in natural or colored upon specific customer requirements.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneloy® D A8 | PMMA medium flow, high mechanical strength, for transparent and solid colors. | 1,16 - 1,18 g/cm3 | 7 gr/10' | 2 Kj/m2 | HB YC | |
| Dafneloy® D A9 | PMMA low flow, high mechanical strength, for transparent and solid colors. | 1,16 - 1,18 g/cm3 | 3 gr/10' | 2 Kj/m2 | HB YC | |
| Dafneloy® D H | PMMA good impact resistance. | 1,16 g/cm3 | 1,5 gr/10' | 6 Kj/m2 | HB |
Xelter® V
Dynamically Vulcanized TPE’s for Injection Molding, Extrusion, Blow Molding and Calendering. Overmolding and Coextrusion onto PP and PP compounds. Hardnesses from 35 Sh A to 50 Sh D. Easy coloring and easy processing grades. Flame retardant grades. Food contact grades. Custom developed grades.| Name | Type | Hardness Shore A ISO 868 | Density ISO 1183 1/A | |
|---|---|---|---|---|
| Xelter® V 410/420A35-XXX-YYY | TPV-(PP+EPDM) | 35 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A40-XXX-YYY | TPV-(PP+EPDM) | 40 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A40-XXX-YYY-G2 | TPV-(PP+EPDM) | 40 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A50-XXX-YYY | TPV-(PP+EPDM) | 50 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A60-XXX-YYY | TPV-(PP+EPDM) | 60 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A60-XXX-YYY-E1 | TPV-(PP+EPDM) | 60 3s | 0,95 g/cm3 | |
| Xelter® V 410/420A60-XXX-YYY-G1 | TPV-(PP+EPDM) | 60 3s | 0,95 g/cm3 | |
| Xelter® V 410/420A65-XXX-YYY-G2 | TPV-(PP+EPDM) | 65 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A70-XXX-YYY | TPV-(PP+EPDM) | 70 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A70-XXX-YYY-E1 | TPV-(PP+EPDM) | 70 3s | 0,95 g/cm3 | |
| Xelter® V 410/420A70-XXX-YYY-G1 | TPV-(PP+EPDM) | 70 3s | 0,95 g/cm3 | |
| Xelter® V 410/420A80-XXX-YYY | TPV-(PP+EPDM) | 80 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A90-XXX-YYY | TPV-(PP+EPDM) | 90 3s | 0,90 g/cm3 | |
| Xelter® V 410/420A90-XXX-YYY-E1 | TPV-(PP+EPDM) | 90 3s | 0,95 g/cm3 | |
| Xelter® V 410/420D40-XXX-YYY | TPV-(PP+EPDM) | 40 3s | 0,90 g/cm3 | |
| Xelter® V 430A90-XXX-YYY | TPV-(PP+EPDM) | 90 3s | 0,90 g/cm3 | |
| Xelter® V 430D40-XXX-YYY | TPV-(PP+EPDM) | 40 3s | 0,90 g/cm3 |
Xelter® tech
Grades for Overmolding and Coextrusion onto polar engineering plastics. Custom developed grades.| Name | Type | Hardness Shore A ISO 868 | Density ISO 1183 1/A | |
|---|---|---|---|---|
| Xelter® tech A11/A21A50-XXX-YYY | Hybrid & High-Tech | 50 3s | 1,02 g/cm3 | |
| Xelter® tech A11/A21A65-XXX-YYY | Hybrid & High-Tech | 65 3s | 1,04 g/cm3 | |
| Xelter® tech A11/A21A70-XXX-YYY | Hybrid & High-Tech | 70 3s | 1,06 g/cm3 | |
| Xelter® tech B11/B21A60-XXX-YYY | Hybrid & High-Tech | 60 3s | 1,04 g/cm3 | |
| Xelter® tech B11/B21A70-XXX-YYY | Hybrid & High-Tech | 70 3s | 1,08 g/cm3 | |
| Xelter® tech B11/B21A80-XXX-YYY | Hybrid & High-Tech | 80 3s | 1,08 g/cm3 | |
| Xelter® tech E11/E21A35-XXX-YYY-E1 | Hybrid & High-Tech | 35 3s | 0,95 g/cm3 | |
| Xelter® tech E11/E21A40-XXX-YYY | Hybrid & High-Tech | 40 3s | 0,98 g/cm3 | |
| Xelter® tech E11/E21A40-XXX-YYY-E1 | Hybrid & High-Tech | 40 3s | 0,95 g/cm3 | |
| Xelter® tech E11/E21A45-XXX-YYY-G1 | Hybrid & High-Tech | 45 3s | 0,95 g/cm3 | |
| Xelter® tech E13/E23A35-XXX-YYY-G1 | Hybrid & High-Tech | 35 3s | 1,20 g/cm3 | |
| Xelter® tech E13/E23A40-XXX-YYY-G1 | Hybrid & High-Tech | 40 3s | 1,20 g/cm3 |
Dafneblend®
Compounds available in a wide range of different polymers alloys. Our portfolio includes reinforced grades; halogen or halogen-free flame retardant grades, UL94 certified. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | Vicat B/50 ISO 306 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneblend® PK 202/L | Blend PA/ABS with high flow and good mechanical properties. UV stabilized. | 1,06 g/cm3 | 115 °C | 50 Kj/m2 | HB | |
| Dafneblend® PM 200 | Blend ABS/PC general purpose, good flow properties. | 1,10 - 1,12 g/cm3 | 110 °C | 30 Kj/m2 | HB YC | |
| Dafneblend® PM 500 | Blend PC/ABS general purpose, good flow properties and good impact resistance. | 1,13 - 1,15 g/cm3 | 118 °C | 35 Kj/m2 | HB YC | |
| Dafneblend® PM 700 | Blend PC/ABS general purpose, good flow properties, good impact and heat resistance. | 1,15 - 1,16 g/cm3 | 129 °C | 55 Kj/m2 | HB YC | |
| Dafneblend® PM 750XF | Blend PC/ABS flame retardant UL94 V1 1,5mm, halogen free, ball pressure test 125°C. | 1,16 g/cm3 | 130 °C | 50 Kj/m2 | V1 |
| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneblend® PM 700XF | Blend PC/ABS flame retardant UL94 V0 1,5 mm, halogen free. | 1,18 g/cm3 | 2300 MPa | 50 Kj/m2 | V0 YC | |
| Dafneblend® PL 200/E | Blend PC/PBT impact modified, good mechanical resistance. | 1,22 g/cm3 | 2200 MPa | 50 Kj/m2 | HB | |
| Dafneblend® PL 300/EC | Blend PC/PBT impact modified, good chemical resistance. | 1,18 g/cm3 | 1600 MPa | 60 Kj/m2 | HB | |
| Dafneblend® PL 706 | Blend PC/PBT 30% glass fiber, low warpage, good chemical resistance. | 1,47 - 1,49 g/cm3 | 8000 MPa | 10 Kj/m2 | HB |
| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneblend® PK 201 | Blend PA/ABS good mechanical properties, good chemical resistance. | 1,07 g/cm3 | 30 gr/10' | 60 Kj/m2 | HB YC | |
| Dafneblend® PK 202 | Blend PA/ABS high flowability and good mechanical properties, good chemical resistance. | 1,06 g/cm3 | 55 gr/10' | 50 Kj/m2 | HB YC | |
| Dafneblend® PX 200 L | Blend PC/ASA good UV and weathering resistance, good impact strength. | 1,10 - 1,13 g/cm3 | 12 gr/10' | 30 Kj/m2 | HB | |
| Dafneblend® PX500 L | Blend PC/ASA good UV and weathering resistance, high heat resistance, good impact strength. | 1,13 - 1,16 g/cm3 | 20 g/10' | 40 Kj/m2 | HB |
Dafnelan®
Compounds based on copolymer or homopolymer acetal resin (POM) with high stiffness and an outstanding wear resistance. Our products are available glass fiber reinforced; impact modified and lubricated with Silicon, PTFE or Molybdenum Disulfide. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnelan® LR2 | POM OMO general purpose, high viscosity. | 1,42 g/cm3 | 2 gr/10' | 15 Kj/m2 | HB | |
| Dafnelan® LR12 | POM OMO general purpose, medium viscosity. | 1,40 g/cm3 | 12 gr/10' | 9 Kj/m2 | HB | |
| Dafnelan® LR9 P03/E | POM OMO 15% glass fibers, medium viscosity, high stiffness, low warpage. | 1,50 g/cm3 | 8 gr/10' | 5 Kj/m2 | HB | |
| Dafnelan® GR9 T02 | POM COP PTFE modified. | 1,45 g/cm3 | 9 gr/10' | 5 Kj/m2 | HB | |
| Dafnelan® GR9 T04 | POM COP PTFE modified | 1,48 - 1,50 g/cm3 | 9 gr/10' | 5 Kj/m2 | HB | |
| Dafnelan® GR9 MS1 | POM COP lubricated MoS2. | 1,40 g/cm3 | 10 gr/10' | 6 Kj/m2 | HB |
Dafnetec®
High Performance Polyphenylene Sulfide Compounds (PPS) with high thermal and chemical resistance. Good fire resistance. The products can be glass and carbon fiber reinforced and mineral filled. They can be colored upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnetec® PPS P08 | PPS 40% glass fiber, flame retardante UL94 V0 1,6mm. | 1,66/1,68 g/cm3 | 15200 MPa | 10 Kj/m2 | V0 | |
| Dafnetec® PPS G12 | PPS glass fiber and mineral filler, flame retardante UL94 V0 1,6mm. | 1,96/1,98 g/cm3 | 17500 MPa | 11 Kj/m2 | V0 |
Dafnetherm®
Thermal conductive compounds based on different polymers. Various fillers can be added to increase thermal properties based on customer requests.| Name | Compound | Surface Resistivity IEC 93 | Thermal conductivity ISO 22007-2 - In-Plane | Thermal conductivity ISO 22007-2 - Through-Plane | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnetherm® PPGR16 | Crystalline carbon additive, thermal conductive, electrical conductive. | 1E3 Ohm | 3 W/(m*K) | 10 W/(m*K) | HB | |
| Dafnetherm® PPBN16 | Inorganic filler, thermal conductive, electrical insulating. | > 1E12 Ohm | 1,4 W/(m*K) | 9 W/(m*K) | HB |
Dafneohm®
Electrically conductive and dissipative compounds based on various resins, available in a wide range of grades. Different fillers or additives can be added to meet the requested customer conductive properties. They can be colored upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Surface Resistivity IEC 60093 | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneohm® 6A KP06 | PA6 reinforced, electrically conductive. | 1,32/1,34 g/cm3 | 14000 MPa | 5E03 Ohm | HB | |
| Dafneohm® EC CB 4 | PP electrically conductive. | 1,02 g/cm3 | 1000 MPa | 3E04 Ohm | HB | |
| Dafneohm® EH K22_D | PP reinforced, electrically conductive. | 1 g/cm3 | 8000 MPa | 1E02 Ohm | HB |
Dafnemid®
Compounds based on polyamide 6 and 66 (PA6 – PA66), with good heat resistance and good mechanical properties. Our portfolio includes different grades, reinforced with glass and carbon fiber or mineral filled; impact modified, lubricated with Silicon, PTFE or Molybdenum disulfide; halogen or halogen-free flame retardant base, UL94 listed. Our products can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnemid® 6A P06 | PA6 30% glass fiber reinforced. | 1,36 g/cm3 | 8000 MPa | 12 Kj/m2 | HB YC | |
| Dafnemid® 6A MS1 | PA6 lubricated with MoS2. | 1,14 g/cm3 | 2600 MPa | 5 Kj/m2 | HB | |
| Dafnemid® 6XA P04 | PA6 20% glass fiber, flame retardant UL94 V0 1,7 mm, with halogen. | 1,54 g/cm3 | 6800 MPa | 6 Kj/m2 | V0 YC - GWFI 960, GWIT 850 | |
| Dafnemid® 66A K04 | PA66 20% carbon fiber. | 1,22 g/cm3 | 12000 MPa | 5 Kj/m2 | HB | |
| Dafnemid® 66A MS1 | PA66 lubricated MoS2. | 1,10/1,12 g/cm3 | 2000 MPa | 7 Kj/m2 | HB | |
| Dafnemid® 66A T04 | PA66 lubricated Teflon. | 1,26 g/cm3 | 2800 MPa | 4 Kj/m2 | HB | |
| Dafnemid® 66XA P05/T | PA66 25% glass fiber, heat stabilized, flame ritardant UL94 V0 0,8 mm, with halogens. | 1,50/1,55 g/cm3 | 8500 MPa | 9 Kj/m2 | V0 YC - GWFI 960 - GWIT 875 - RTI 140 | |
| Dafnemid® 6A | PA6 medium viscosity. | 1,13 g/cm3 | 2700 MPa | 4 Kj/m2 | V2 | |
| Dafnemid® 6A P12/T | PA6 60% glass fiber, very high rigidity and strength, heat stabilized. | 1,70 g/cm3 | 19000 MPa | 16 Kj/m2 | HB |
Dafneloy® M
Polycarbonate Compounds (PC) offering a good combination of toughness, impact strength and high heat resistance. Our products can be glass fiber reinforced and impact modified. They are UL94 certified for flame retardance, available both halogenated and halogen-free base. They can be colored upon specific customer requirements, also in transparent colors.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafneloy® M A | PC low viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,20 g/cm3 | 20 gr/10' | 55 Kj/m2 | HB | |
| Dafneloy® M B | PC medium viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,20 g/cm3 | 12 gr/10' | 65 Kj/m2 | HB | |
| Dafneloy® M C | PC high viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,2 g/cm3 | 8 gr/10' | 70 Kj/m2 | HB | |
| Dafneloy® M XF | PC flame retardant, halogen free, UL94 V0 1,6 mm. | 1,2 g/cm3 | 10 gr/10' | 60 Kj/m2 | V0 YC | |
| Dafneloy® M XF EA | PC flame retardant, halogen free, UL94 V0 1,0 mm, impact modified. | 1,18 g/cm3 | 8 gr/10' | 70 Kj/m2 | V0 YC | |
| Dafneloy® M XA P02 | PC 10% glass fiber reinforced, flame retardant, with halogens, UL94 V0 1,6 mm. | 1,26/1,30 g/cm3 | 10 gr/10' | 10 Kj/m2 | V0 YC | |
| Dafneloy® M XF P02 | PC 10% glass fiber reinforced, flame retardant, halogen free, UL94 V0 1,6 mm. | 1,26/1,30 g/cm3 | 10 gr/10' | 7 Kj/m2 | V0 YC | |
| Dafneloy® M A/L | PC low viscosity, good mechanical and high heat resistance, UV stabilized, for transparent and solid colors. | 1,20 g/cm3 | 20 gr/10' | 55 Kj/m2 | HB |
Dafnelac®
Styrenic Compound (ABS-SAN-ASA) available in different grades in a wide range of melt flow rates, impact and heat resistance, in accordance with market demands and industry standards. Some products are available glass fiber reinforced; HB class and halogen-based flame retardant with UL94 certification. They can be tailor made colored, upon specific customer requirements, with high or low gloss.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnelac® SF/A BLACK S4F | High flow, general purpose. Black color. Antistatic. | 1,04 g/cm3 | 34 g/10' | 18 Kj/m2 | HB | |
| Dafnelac® SF/B DARK COLOR MATT | ABS good flow, low gloss appearance. Antistatic. UV stabilized. | 1,04 g/cm3 | 30 g/10' | 10 Kj/m2 | HB | |
| Dafnelac® FXC NEUTRO/T | ABS with goog heat resistance, good processability. Flame retardant grade with halogens. | 1,20 g/cm3 | 25 g/10' | 10 Kj/m2 | - | |
| Dafnelac® SF/B MET | ABS high flow, general purpose, metallized colour. Antistatic. UV stabilized. | 1,04 g/cm3 | 35 g/10' | 12 Kj/m2 | HB | |
| Dafnelac® SF/A | ABS high flow, general purpose, antistatic, good impact resistance. | 1,04 g/cm3 | 35 gr/10' | 16 KJ/m2 | HB YC | |
| Dafnelac® KE | ABS low flow, high impact resistance, suitable for extrusion and vacuumforming. | 1,04 g/cm3 | 5 gr/10' | 25 Kj/m2 | HB | |
| Dafnelac® SN | ABS medium flow, general purposes, good impact resistance. | 1,04 g/cm3 | 26 gr/10' | 17 Kj/m2 | HB YC | |
| Dafnelac® SF | ABS high flow, general purpose, good impact resistance. | 1,04 g/cm3 | 35 gr/10' | 16 Kj/m2 | HB YC | |
| Dafnelac® SN AC | ABS medium flow, improved chemical resistance. | 1,04 g/cm3 | 20 gr/10' | 20 Kj/m2 | HB YC | |
| Dafnelac® TM | ABS medium heat resistance Vicat B/50 100°C. | 1,05 g/cm3 | 16 gr/10' | 12 Kj/m2 | HB YC | |
| Dafnelac® TH | ABS high heat resistance Vicat B/50 102°C. | 1,05 g/cm3 | 13 gr/10' | 12 Kj/m2 | HB YC | |
| Dafnelac® TX | ABS very high heat resistance Vicat B/50 110°C. | 1,05 g/cm3 | 6 gr/10' | 11 Kj/m2 | HB | |
| Dafnelac® FXC | ABS flame retardant, UL94 V0 - 5VA on 1,7mm. | 1,18 - 1,20 g/cm3 | 40 gr/10' | 11 Kj/m2 | V0 - 5VA YC | |
| Dafnelac® FXC T | ABS flame retardant, with improved heat resistance, UL94 V0 - 5VA on 1,7mm. | 1,2 g/cm3 | 25 gr/10' | 10 Kj/m2 | V0 - 5VA YC | |
| Dafnelac® AS3/LT | ASA improved thermal resistance, good chemical, UV and weathering resistance. | 1,07 g/cm3 | 10 gr/10' | 12 Kj/m2 | HB YC | |
| Dafnelac® NRP | SAN general purpose for injection moulding, for transparent and solid colors. | 1,07 g/cm3 | 15 gr/10' | 2 Kj/m2 | HB | |
| Dafnelac® NRP P04 | SAN 20% glass fiber reinforced. | 1,22 g/cm3 | 9 gr/10' | 3 Kj/m2 | HB | |
| Dafnelac® SF/B ATX | ABS high flow and good mechanical properties. Antistatic. UV stabilized. For food compliance uses. | 1,04 g/cm3 | 35 gr/10' | 16 KJ/m2 | HB YC | |
| Dafnelac® SF/B | ABS high flow, general purpose, good impact resistance, antistatic and UV stabilized. | 1,04 g/cm3 | 35 gr/10' | 16 KJ/m2 | HB YC | |
| Dafnelac® AS2B | ASA high flow, good mechanical properties. Antistatic. UV stabilized. | 1,07 g/cm3 | 30 gr/10' | 10 KJ/m2 | HB YC | |
| Dafnelac® FXC B | ABS flame retardant, UL94 V0 – 5VA on 1,7mm, antistatic and UV stabilized. | 1,18 - 1,20 g/cm3 | 40 gr/10' | 11 KJ/m2 | V0 - 5VA YC |
Dafnestil®
Styrenic Compound (PS) available in different grades, impact and heat resistance in accordance with the industry standards of household appliances and electric market. Some products are available halogen-based flame retardant. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Dafnestil® KU | GPPS good fluidity and good heat resistance. | 1,05 g/cm3 | 10 gr/10' | 1,7 Kj/m2 | HB | |
| Dafnestil® AM | HIPS medium impact, good heat resistance and high stiffness. | 1,04 g/cm3 | 10 gr/10' | 5 Kj/m2 | HB | |
| Dafnestil® AT | HIPS high impact, heat resistant and high stiffness. | 1,04 g/cm3 | 5 gr/10' | 6 Kj/m2 | HB | |
| Dafnestil® AXR | HIPS high impact, flame retardant UL94 V0 1,6mm - GWFI 960 2,00mm. | 1,14/1,18 g/cm3 | 10 gr/10' | 6 Kj/m2 | V0 - GWFI 960 | |
| Dafnestil® AXB | HIPS high impact, flame retardant UL94 V2 1,6mm - GWFI 850 1,00mm. | 1,10/1,12 g/cm3 | 12 gr/10' | 6 Kj/m2 | V2 1,6mm - GWFI 850 | |
| Dafnestil® AXE | HIPS high impact, flame retardant UL94 V2 1,6mm - GWFI 960 1,00mm. | 1,17 g/cm3 | 6 gr/10' | 5 Kj/m2 | V2 1,6mm - GWFI 960 | |
| Dafnestil® AXF | HIPS high impact, flame retardant UL94 V2 1,6mm - GWFI 750 1,00mm. | 1,14/1,17 g/cm3 | 7 gr/10' | 5 Kj/m2 | V2 1,6mm - GWFI 750 |
Isoplen®
Homopolymer and Copolymer Polypropylene Compound with high mechanical properties, developed in accordance with market demands and industry standards. Products available in a wide range of colors and certified flame retardant versions available both halogenated and halogen-free.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoplen® A H F | PP homo, natural colour medium flowability | 12 g/10' | 1400 MPa | 3,3 Kj/m2 | Classe HB | |
| Isoplen® H2 T V | PP homo, natural colour, heat stabilized, high flowability | 20 g/10' | 1400 MPa | 5 Kj/m2 | Classe HB | |
| Isoplen® A K F | PP copo, medium flowability | 13 g/10' | 1300 MPa | 11 Kj/m2 | Classe HB | |
| Isoplen® A K Z | PP copo, high flowability | 21 g/10' | 1350 MPa | 5,6 Kj/m2 | Classe HB | |
| Isoplen® FR V2 | PP copo flame retardant low halogen content | 10 g/10' | 1400 MPa | 10 Kj/m2 | Classe V2 YC | |
| Isoplen® HK X V0 HF | Unfilled. Heat stabilized. Flame Retardant grade without halogens. | 10 g/10' | 1600 Mpa | 3,5 KJ/m2 | Classe V0 YC |
Isoflex®
Copolymer Polypropylene, unfilled and not stabilized.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoflex® C800 | Polypropylene copolymer. | 6 g/10' | 800 Mpa | 45 KJ/m2 | / |
Isodur®
Polyesters compounds (PBT) available in different grades, high heat and chemical resistant, good dimension stability. Our products can be glass fiber reinforced; halogen-based flame retardant, UL94 certified. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isodur® A 15 10 GF20 | PBT 20% glass fiber reinforced. | 1,45 g/cm3 | 5500 MPa | 7 Kj/m2 | HB | |
| Isodur® A 15 10 GF30 | PBT 30% glass fiber reinforced. | 1,56 g/cm3 | 8500 MPa | 8 Kj/m2 | HB | |
| Isodur® 15 10 GF20 V0 | PBT 20% glass fiber reinforced, flame retardant UL94 V0 1,5mm. | 1,57/1,59 g/cm3 | 7000 MPa | 7 Kj/m2 | V0 YC |
Isofil®
Standard and High Performance Modified Polypropylene with different mineral fillers (T/TC/CaCO3/BaSO4/Mica) in accordance with market demands and industry standards. Products with application features in colors and specifications developed with customers. Certified flame retardant versions are available both halogenated and halogen-free.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isofil® H 20 TP X | PP homo 20% talc natural colour | 9 g/10' | 2600 MPa | 3 Kj/m2 | Classe HB | |
| Isofil® H 40 TP F | PP homo 40% talc | 12 g/10' | 4000 MPa | 2,4 Kj/m2 | Classe HB | |
| Isofil® K 20 TP X | PP copo 20% talc | 10 g/10' | 2000 MPa | 7 Kj/m2 | Classe HB | |
| Isofil® K 40 TP V | PP copo 40% talc | 20 g/10' | 3400 MPa | 4,2 Kj/m2 | Classe HB | |
| Isofil® HK 10 TVHM | 10% micro talc filled polypropylene. | 20 g/10' | 2400 MPa | 4 Kj/m2 | Classe HB YC | |
| Isofil® HK 30 TVH0 | 30% talc filled homopolymer polypropylene. | 20 g/10' | 3400 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 35 GVH0 | 35% talc filled copolymer polypropylene. | 21 g/10' | 3100 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® K 40 T | 40% talc filled polypropylene. | 7 g/10' | 4200 Mpa | 2,6 KJ/m2 | Classe HB | |
| Isofil® K 20 T xxx HB | 20% talc filled copolymer polypropylene. | 16 g/10' | 2300 Mpa | 6,5 KJ/m2 | Classe HB YC | |
| Isofil® HK 20 TCH0 | 20% mineral filled polypropylene. Heast stabilized. | 6 g/10' | 2300 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 20 TFH0 | 20% mineral filled polypropylene. Heat stabilized. | 13 g/10' | 2300 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® K 40 T xxx HB | 40% talc filled copolymer polypropylene. Heat stabilized. | 8 g/10' | 3800 Mpa | 2,6 KJ/m2 | Classe HB YC | |
| Isofil® HK 30 TSH1 | 30% talc filled polypropylene homopolymer. Heat stabilized. | 3 g/10' | 3500 Mpa | 5 KJ/m2 | Classe HB YC | |
| Isofil® H 40 C2 F | 40% calcium carbonate filled homopolymer polypropylene. | 13 g/10' | 2500 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 30 TTH1 | 30% talc filled polypropylene. UV stabilized. Heat stabilized. | 3 g/10' | 3400 Mpa | 2,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 30 TXH0 | 30% talc filled polypropylene. Heat stabilized. | 8 g/10' | 3300 Mpa | 2,7 KJ/m2 | Classe HB YC | |
| Isofil® HK 40 2FH0 | 40% calcium carbonate filled polypropylene. Heat stabilized. | 13 g/10' | 2500 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 40 5FH0 | 40% calcium carbonate polypropylene. | 13 g/10' | 2500 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 40 TTH0 | 40% talc filled homopolymer polypropylene. Heat stabilized. | 4 g/10' | 3800 Mpa | 2,4 KJ/m2 | Classe HB YC | |
| Isofil® HK 50 C2 V | 50% calcium carbonate homopolymer polypropylene. Heat stabilized. | 18 g/10' | 3100 Mpa | 2,5 KJ/m2 | Classe HB YC | |
| Isofil® HK 30 TFH2 | 30% talc filled polypropylene. | 14 g/10' | 34600 Mpa | 3,8 KJ/m2 | Classe HB YC | |
| Isofil® HK 20 TFHH | 20% talc filled polypropylene. Heat stabilized. Detergent Resistant. | 5 g/10' | 2200 Mpa | 3,9 KJ/m2 | Classe HB YC | |
| Isofil® H 40 C2 X | 40% calcite filled homopolymer polypropylene. | 9 g/10' | 2400 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 25 TVH0 | 25% talc filled copolymer polypropylene. | 23 g/10' | 1800 Mpa | 7 KJ/m2 | Classe HB YC | |
| Isofil® HK 40 TVH0 | 40% talc filled copolymer polypropylene. | 18 g/10' | 4000 Mpa | 3 KJ/m2 | Classe HB YC | |
| Isofil® HK 30 TVH2 | 30% talc filled polypropylene. | 16 g/10' | 3200 Mpa | 3,3 KJ/m2 | Classe HB YC | |
| Isofil® HK 50 2FH0 | 50% calcium carbonate filled polypropylene. | 20 g/10' | 2800 Mpa | 3,5 KJ/m2 | Classe HB | |
| Isofil® HK 30 TTH0 | 30% talc polypropylene. | 4 g/10' | 3300 Mpa | 3,1 KJ/m2 | Classe HB YC | |
| Isofil® K 0 T xxx HB | Copolymer polypropylene. | 17 g/10' | 1200 Mpa | 7,9 KJ/m2 | Classe HB YC | |
| Isofil® HK 25 GVH | 25% talc filled copolymer polypropylene. | 16 g/10' | 2200 Mpa | 5,1 KJ/m2 | Classe HB YC | |
| Isofil® HK 20 2VH0 | 20% calcium carbonate polypropylene. Heat stabilized. | 16 g/10' | 1850 Mpa | 2,4 KJ/m2 | Classe HB YC | |
| Isofil® HK 25 GVH1 | 25% talc copolymer polypropylene. Heat stabilized. | 17 g/10' | 2000 Mpa | 12,9 KJ/m2 | Classe HB YC | |
| Isofil® KPZ 4001D | 20% talc filled copolymer polypropylene. Heat stabilized. | 20 g/10' | 2400 Mpa | 4,7 KJ/m2 | Classe HB YC | |
| Isofil® RV 4603S | 20% talc filled impact modified polypropylene. Compliant to TL 52388-F. UV stabilized. Scratch Resistant. | 18 g/10' | 2000 Mpa | 35 KJ/m2 | Classe HB | |
| Isofil® MV 4509Y | 20% talc filled polypropylene copolymer. Impact modified. UV stabilized. Scratch Resistant. | 26 g/10' | 1900 Mpa | 30 KJ/m2 | Classe HB | |
| Isofil® K 20 T 48.450 AFU | 20% talc filled copolymer polypropylene. Impact modified and scratch resistant. UV stabilized. | 19 g/10' | 1700 Mpa | 45 KJ/m2 | Classe HB | |
| Isofil® MF 4124S | 20% talc filled polypropylene compound. It exhibits high stiffness and low emission properties. Scratch Resistant. | 15 g/10' | 2700 Mpa | 4 KJ/m2 | Classe HB | |
| Isofil® MY 2205Y | 10% talc filled copolymer polypropylene. Low emission grade. Scratch Resistant. | 25 g/10' | 1600 Mpa | 18 KJ/m2 | Classe HB | |
| Isofil® K 10 T 53.180U | 13% talc filled copolymer polypropylene. UV stabilized. Scratch Resistant. | 15 g/10' | 1650 Mpa | 18 KJ/m2 | Classe HB | |
| Isofil® SV 4205Y | 20% talc filled polypropylene copolymer. Good flowability and stiffness. UV stabilized. Scratch Resistant. | 16 g/10' | 2300 Mpa | 6 KJ/m2 | Classe HB | |
| Isofil® RF 3403Y | 15% talc filled polypropylene copolymer. Impact modified. High fluidity. Low CLTE. UV stabilized. Scratch Resistant. | 15 g/10' | 1700 Mpa | 25 KJ/m2 | Classe HB | |
| Isofil® K 10 T 46.400 AFU | 10% talc filled copolymer polypropylene. Scratch resistant. UV stabilized. | 22 g/10' | 1300 Mpa | 40 KJ/m2 | Classe HB | |
| Isofil® H 20 TP F HS | 20% Talc filled polypropylene homopolymer. Low emission. Compliant to VW44045-PP6.Heat stabilized. | 12 g/10' | 2800 Mpa | 3 KJ/m2 | Classe Hb | |
| Isofil® MF 3604Y | 16% talc filled polypropylene. Impact resistance grade. UV stabilized. Scratch Resistant. | 14 g/10' | 1500 Mpa | 30 KJ/m2 | Classe HB | |
| Isofil® MZ 3506Y | 17% talc filled copolymer polypropylene. Good flowability. Low emission. UV stabilized. Heat stabilized. Scratch Resistant. | 22 g/10' | 2000 Mpa | 25 KJ/m2 | Classe HB | |
| Isofil® H 40 TG S HS | 40% talc filled polypropylene homopolymer. | 10 kg/10' | 4100 Mpa | 3,5 KJ/m2 | Classe HB | |
| Isofil® H 20 T F UV | 20% talc filled homopolymer polypropylene. UV stabilized. | 15 g/10' | 2600 Mpa | 2,5 KJ/m2 | Classe HB | |
| Isofil® SF 4303U | 20% talc filled copolymer polypropylene with good stiffness and impact resistance. UV stabilized. | 15 g/10' | 1800 Mpa | 15 KJ/m2 | Classe HB | |
| Isofil® K 30 T 60.90L | 30% talc filled copolymer polypropylene. UV stabilized. | 16 g/10' | 2300 Mpa | 9 KJ/m2 | Classe HB | |
| Isofil® SV 4118X | 20% talc filled homopolymer polypropylene. Compliant to TL 52658-WD01. UV stabilized. Heat stabilized. | 16 g/10' | 2800 Mpa | 2,5 KJ/m2 | Classe HB | |
| Isofil® PZ 8103H | 40% talc filled polypropylene homopolymer. Heat stabilized. | 20 g/10' | 4300 Mpa | 3 KJ/m2 | Classe HB | |
| Isofil® HF 6205X | 30% talc filled copolymer polypropylene. UV stabilized. Heat stabilized. | 14 g/10' | 2300 Mpa | 6 KJ/m2 | Classe HB | |
| Isofil® SW 4909U | 20% talc filled copolymer polypropylene. Impact modified grade with high flowability. UV stabilized. | 40 g/10' | 1500 Mpa | 40 KJ/m2 | Classe HB | |
| Isofil® K 20 T 50.400LCE SR AF | 17% talc filled copolymer polypropylene. Low CLTE and scratch resistant. UV stabilized. | 32 g/10' | 1450 Mpa | 40 KJ/m2 | Classe HB | |
| Isofil® SF 4501Y | 20% talc filled copolymer polypropylene. Impact modified grade. UV stabilized. Scratch Resistant. | 14 g/10' | 1900 Mpa | 20 KJ/m2 | Classe HB | |
| Isofil® K 30 T 50.200LCE SR AF | 30% talc filled copolymer polypropylene. High impact. Scratch resistant. High fluidity. UV stabilized. | 33 g/10' | 1700 Mpa | 20 KJ/m2 | Classe HB | |
| Isofil® PF 4102H | 20% Talc filled polypropylene homopolymer. Low emission. Compliant to VW44045-PP6 and WSS-M4D729-B1. Heat stabilized. | 12 g/10' | 2800 Mpa | 3 KJ/m2 | Classe HB | |
| Isofil® HK 20 TP F HS | 20% talc filled copolymer polypropylene. | 12 g/10' | 2200 Mpa | 6 KJ/m2 | Classe HB | |
| Isofil® HF 2206H L | 10% talc filled polypropylene copolymer. Heat stabilized. Laserable. | 12 g/10' | 1500 Mpa | 8 KJ/m2 | Classe HB | |
| Isofil® HK 20 T V0 | 20% talc filled copolymer polypropylene. Heat stabilized. Flame Retardant grade With halogens | 6 g/10' | 2900 Mpa | 3,5 KJ/m2 | Classe HB | |
| Isofil® H 40 TG X HS | 40% talc filled homopolymer polypropylene. Compliant to VW 44045-PP8. Heat stabilized. | 15 g/10' | 4000 Mpa | 2,5 KJ/m2 | Classe HB | |
| Isofil® MZ 2102H | 10% talc filled homopolymer polypropylene. Low emission grade. | 25 g/10' | 2350 Mpa | 3,5 KJ/m2 | Classe HB | |
| Isofil® KGF 4002U | 21,5% talc filled copolymer polypropylene. UV stabilized. | 12 g/10' | 2000 Mpa | 4 KJ/m2 | Classe HB | |
| Isofil® HK 25 6VH | 25% talc-calcium carbonate filled polypropylene. | 16 g/10' | 2400 Mpa | 5 KJ/m2 | Classe HB YC | |
| Isofil® HZ 9101D | 40% talc filled homopolymer polypropylene. Good flowability. | 23 g/10' | 4100 Mpa | 2,5 KJ/m2 | Classe HB | |
| Isofil® MC 4214Y | 20% talc filled copolymer polypropylene. UV stabilized. Scratch Resistant. | 8 g/10' | 2300 Mpa | 7 KJ/m2 | Classe HB |
Isoglass®
Polypropylene Reinforced with Glass Fiber, chemically coupled or mechanical, with high thermal, impact and stiffness properties, aligned with the standards of the automotive and household appliance industries.The products are available in the color range and flame retardant grades indicated by the sectors with relevant certifications both halogenated and halogen-free.
| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoglass® H 30 FVL C | PP homo 30% glass fiber. Heat stabilized. | 6 g/10' | 5800 MPa | 11,5 Kj/m2 | Classe HB YC | |
| Isoglass® H 20 FVL X | 20% glass fiber polypropylene. Heat stabilized. | 8 g/10' | 3900 Mpa | 7,4 KJ/m2 | Classe HB YC | |
| Isoglass® HGV 6002D | 30% glass fiber homopolymer polypropylene. Heat stabilized. Detergent Resistant. | 17 g/10' | 5600 Mpa | 9,1 KJ/m2 | Classe HB YC | |
| Isoglass® H3V 6009D | 30% talc filled and glass fiber reinforced polypropylene homopolymer. Heat stabilized. Detergent resistant. | 17 g/10' | 4700 Mpa | 5 KJ/m2 | Classe HB YC | |
| Isoglass® H 20 CGF X HS | 20% chemically coupled glass fiber reinforced homopolymer polypropylene. Compliant to VW 44045-PP9. Heat stabilized. | 8 g/10' | 4000 Mpa | 7 KJ/m2 | Classe HB | |
| Isoglass® H 30 CGF C UV | 30% chemically coupled glass fiber reinforced polypropylene. Low odor and emission. Compliant to VW44045-PP10 and VW50180. UV stabilized. Heat stabilized. | 5 g/10' | 5800 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® K 30 CGF X | 30% glass fiber reinforced copolymer polypropylene. | 8 g/10' | 4000 Mpa | 16 KJ/m2 | Classe HB | |
| Isoglass® 4F 4030U | 22% chemically coupled glass fiber and mineral filled reinforced polypropylene copolymer. Good stiffness and impact strenght balance combined with high flowability. UV stabilized. | 14 g/10' | 3200 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® H 30 CGF F UV | 30% glass fiber reinforced homopolymer polypropylene. UV stabilized. | 13 g/10' | 5000 Mpa | 8 KJ/m2 | Classe HB | |
| Isoglass® ST 8020N | 40% chemically coupled glass fiber reinforced polypropylene homopolymer. UV stabilized. Heat stabilized. | 4 g/10' | 8000 Mpa | 10 KJ/m2 | Classe HB | |
| Isoglass® H 30 CGF S HS | 30% glass fiber reinforced homopolymer polypropylene. Heat stabilized. | 5 kg/10' | 6000 Mpa | 10 KJ/m2 | Classe HB | |
| Isoglass® SC 6029X | 30% chemically coupled glass fiber reinforced copolymer polypropylene. UV stabilized. Heat stabilized. | 5 g/10' | 4500 Mpa | 22 KJ/m2 | Classe HB | |
| Isoglass® H 30 GFT3 C HS | 30% glass fiber and talc filled polypropylene. Compliant to MS-55246 PP130.50. Heat stabilized. | 8 g/10' | 4500 Mpa | 7 KJ/m2 | Classe HB | |
| Isoglass® HGV 6003X | 30% chemically coupled glass fiber reinforced polypropylene. High flowability. UV stabilized. Chemical Resistant. | 20 g/10' | 5500 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® H 30 CGF 140.80 | 30% glass fiber reinforced homopolymer polypropylene. Compliant to MS-55246 PP140.80. Heat stabilized. | 18 g/10' | 5700 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® H 30 CGF C | 30% chemically coupled glass fiber reinforced polypropylene. Heat stabilized. | 5 g/10' | 6000 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® XX 6014D | 30% chemically coupled glass fiber reinforced polypropylene, high stiffness. Heat stabilized. | 8 g/10' | 7000 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® SX 4010H | 20% chemically coupled glass fiber reinforced homopolymer polypropylene. Compliant to Renault-Nissan AS8. Heat stabilized. | 10 g/10' | 4000 Mpa | 8 KJ/m2 | Classe HB | |
| Isoglass® H 30 CGF X HS | 30% chemically coupled glass fiber reinforced polypropylene. Heat stabilized. | 8 g/10' | 6000 Mpa | 10 KJ/m2 | Classe HB | |
| Isoglass® SX 4015X | 20% chemically coupled glass fiber reinforced homopolymer polypropylene. Compliant to VW 44045. UV stabilized. Heat stabilized. | 8 g/10' | 3800 Mpa | 6 KJ/m2 | Classe HB | |
| Isoglass® K 20 CGF X | 20% glass fiber reinforced copolymer polypropylene. | 10 g/10' | 3400 Mpa | 13 KJ/m2 | Classe HB | |
| Isoglass® EV 3007U | 15% chemically coupled glass fiber reinforced polypropylene copolymer. High flowability grade and good aesthetical appearance. UV stabilized. | 18 g/10' | 2600 Mpa | 12 KJ/m2 | Classe HB | |
| Isoglass® H 25 CGF C UV | 25% chemically coupled glass fibre reinforced Polypropylene. Antistatic.UV stabilized. | 6 g/10' | 5400 Mpa | 11 KJ/m2 | Classe HB | |
| Isoglass® H 30 FVL V | 30% glass fiber filled homopolymer polypropylene. | 20 g/10' | 5700 Mpa | 10 KJ/m2 | Classe HB YC | |
| Isoglass® SX 8022H | 40% chemically coupled glass fiber reinforced polypropylene homopolymer. Heat stabilized. | 10 g/10' | 7700 Mpa | 10 KJ/m2 | Classe HB | |
| Isoglass® H 20 CGF X | 20% glass fiber reinforced homopolymer polypropylene. | 8 g/10' | 3800 MPa | 8 Kj/m2 | Classe HB | |
| Isoglass® H 40 CGF C | 40% glass fiber reinforced homopolymer polypropylene. | 7 g/10' | 7600 MPa | 9 Kj/m2 | Classe HB | |
| Isoglass® K 40 CGF C | 40% glass fiber reinforced copolymer polypropylene. | 4 g/10' | 6200 MPa | 15 Kj/m2 | Classe HB |
Isoglass® XT
High Performance Glass Fiber chemically coupled Polypropilene. The properties guaranteed by this range of PPGF are aligned with high performance polymers, however, guaranteeing the characteristics of the PP. These products provide good combination of thermal and mechanical stress combined with high rigidity.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoglass® XT 4001D | 20% chemically coupled glass fiber reinforced polypropylene. | 7 g/10' | 4000 Mpa | 7 KJ/m2 | Classe HB YC | |
| Isoglass® XT 6001D | 30% chemically coupled high performance glass fiber reinforced polypropylene compound. | 5 g/10' | 6800 Mpa | 11 KJ/m2 | Classe HB YC | |
| Isoglass® XT 8008H | 40% chemically coupled high performance glass fiber reinforced polypropylene homopolymer. High stiffness and low emission. | 5 g/10' | 10000 Mpa | 10 KJ/m2 | Classe HB | |
| Isoglass® XT 4007U | 20% chemically coupled high performance reinforced polypropylene homopolymer. High stiffness and low emission. Compliant to DBL 5430. UV stabilized. | 7 g/10' | 6100 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® XT 6010H | 30% chemically coupled high performance glass fiber reinforced polypropylene homopolymer. High stiffness and low emission. | 6 g/10' | 8400 Mpa | 10 KJ/m2 | Classe HB | |
| Isoglass® XT 1003H | 50% chemically coupled high performance glass fiber reinforced polypropylene homopolymer. High stiffness grade. Heat stabilized. | 3,5 g/10' | 13000 Mpa | 9 KJ/m2 | Classe HB | |
| Isoglass® XT 7001H | 35% chemically coupled glass fiber reinforced polypropylene homopolymer. Low flowability grade. Heat stabilized. | 3 g/10' | 8000 Mpa | 12 KJ/m2 | Classe HB | |
| Isoglass® XT 6001H | 30% chemically coupled high performance glass fiber reinforced polypropylene. Heat stabilized. | 3,5 g/10' | 6500 Mpa | 10 KJ/m2 | Classe HB |
Isoglass® LFT
Polypropylene Pultrusion Compound with long fiber for applications with high dimensional stability and high thermal and mechanical performance. The use of PP LFT is mainly required for structural applications where the orientation of long fibers modifies the anisotropic effect, increasing dimensional stability obtaining applications with very high stiffness. The product range is available in different fiber contents even at high concentrations.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoglass® LFT 1001H | PP homo 50% long glass fiber, heat stabilized. | / | 10500 MPa | 29 Kj/m2 | Classe HB | |
| Isoglass® LFT LFT 0603H | 30% chemically coupled long glass fiber reinforced polypropylene compound with very high mechanical properties and heat stabilized. | / | 6300 Mpa | 21 Kj/m2 | Classe HB |
Green Isofil®
Polypropylene with Mineral Filler formulated with partial quantities of post-industrial and post-consumer raw materials. The products are available in accordance with some standards recently introduced by the automotive and appliance sectors.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Green Isofil® HK 40 C F | PP copo 40% calcium carbonate, heat stabilized, detergent resistant. | 20 g/10' | 1900 MPa | 3,3 Kj/m2 | Classe HB | |
| Green Isofil® K 30 T T HS | 30% talc filled polypropylene copolymer. Industrial quality. Heat stabilized. | 3 g/10' | 2200 MPa | 6 Kj/m2 | Classe HB |
Green Isoglass®
Polypropylene with Glass Fiber reinforcement formulated with partial use of post-industrial and post consumer raw materials. The products are available in accordance with some standards recently introduced by the automotive and appliance sectors.| Name | Compound | MFI ISO 1133 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Green Isoglass® H 30 CGF C HS | 30% chemically coupled glass fiber reinforced polypropylene with 30% circular polymer source. Heat stabilized. | 6 g/10' | 4900 MPa | 9 Kj/m2 | Classe HB | |
| Green Isoglass® H 40 CGF X HS | 40% glass fiber reinforced polypropylene. Industrial quality. Heat stabilized. | 10 g/10' | 6000 MPa | 9 Kj/m2 | Classe HB |
Isoblend®
Compounds available in a wide range of different polymers alloys. Our portfolio includes reinforced grades; halogen or halogen-free flame retardant grades, UL94 certified. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | Vicat B/50 ISO 306 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoblend® B 65 | Unfilled PC/ABS alloy. Natural colour. | 1,12 g/cm3 | 120 °C | 40 Kj/m2 | HB | |
| Isoblend® A 45 | Blend ABS/PC general purpose, good flow properties. | 1,10 - 1,12 g/cm3 | 110 °C | 30 Kj/m2 | HB | |
| Isoblend® A 65 | Blend PC/ABS general purpose, good flow properties and good impact resistance. | 1,13 - 1,15 g/cm3 | 118 °C | 35 Kj/m2 | HB | |
| Isoblend® A 85 | Blend PC/ABS general purpose, good flow properties, good impact and heat resistance. | 1,15 - 1,16 g/cm3 | 129 °C | 55 Kj/m2 | HB | |
| Isoblend® A 40 200 V0 | Blend PC/ABS flame retardant UL94 V0 1,5mm, halogen free. | 1,17 g/cm3 | 105 °C | 30 Kj/m2 | V0 YC | |
| Isoblend® A 65 AF UV | Blend PC/ABS, high fluidity, UV stabilized. | 1,12 g/cm3 | 118 °C | 30 KJ/m2 | HB | |
| Isoblend® A 85 AF UV | Blend PC/ABS, high fluidity, UV stabilized. | 1,15 g/cm3 | 129 °C | 50 KJ/m2 | HB | |
| Isoblend® A65 GF20 | Blend PC/ABS 20% glass fiber reinforced. | 1,29 g/cm3 | 130 °C | 9 KJ/m2 | HB | |
| Isoblend® A65 GF17 | Blend PC/ABS, 17% glass fiber reinforced. | 1,29 g/cm3 | 127 °C | 10 KJ/m2 | HB | |
| Isoblend® A 45 PG | Blend ABS/PC, suitable for electroplating application. | 1,08 g/cm3 | 110 °C | 45 KJ/m2 | HB | |
| Isoblend® A 65 PG | Blend PC/ABS, suitable for electroplating application. | 1,11 g/cm3 | 126 °C | 50 KJ/m2 | HB | |
| Isoblend® A 20 500 V0 | Blend PC/ABS flame retardant UL94 V0 1,5mm, halogen free. | 1,17 g/cm3 | 110 °C | 50 KJ/m2 | V0 YC | |
| Isoblend® A 50 UV | Blend PC/ABS, UV stabilized. | 1,12 g/cm3 | 120 °C | 50 KJ/m2 | HB |
| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoblend® AS 15 15 UV | Blend PC/ASA good UV and weathering resistance, high heat resistance, good impact strength. | 1,13 - 1,16 g/cm3 | 15 gr/10' | 20 Kj/m2 | HB | |
| Isoblend® AS 15 15 V0 UV | Blend PC/ASA flame retardant UL94 V0 3,00mm, UV resistance. | 1,17 g/cm3 | 13 gr/10' | 15 Kj/m2 | V0 |
Isoform®
Compounds based on copolymer or homopolymer acetal resin (POM) with high stiffness and an outstanding wear resistance. Our products are available glass fiber reinforced; impact modified and lubricated with Silicon, PTFE or Molybdenum Disulfide. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoform® A K 03 | POM COP general purpose, high viscosity. | 1,41 g/cm3 | 3 gr/10' | 8 Kj/m2 | HB | |
| Isoform® A K 09 | POM COP general purpose, medium viscosity. | 1,41 g/cm3 | 9 gr/10' | 7 Kj/m2 | HB | |
| Isoform® A K 13 | POM COP general purpose, medium viscosity. | 1,41 g/cm3 | 13 gr/10' | 6 Kj/m2 | HB | |
| Isoform® A K 27 | POM COP general purpose, low viscosity. | 1,41 g/cm3 | 27 gr/10' | 6 Kj/m2 | HB | |
| Isoform® A K 45 | POM COP general purpose, very low viscosity. | 1,41 g/cm3 | 45 gr/10' | 4 Kj/m2 | HB | |
| Isoform® A K 09 GF25 | POM COP 25% glass fiber. | 1,59 g/cm3 | 4 gr/10' | 6 Kj/m2 | HB | |
| Isoform® A K 09 STZ | POM COP impact modified. | 1,37 g/cm3 | 11 gr/10' | 15 Kj/m2 | HB |
Isoryl®
Compounds of Polyphenylene Oxide (PPO), high thermal resistance, good dimensional and hydrolytic stability. The products can be glass fiber reinforced and mineral filled; halogen-free flame retardant, UL94 certified. They can be colored upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoryl® A 137 | PPO Unfilled. | 1,06 g/cm3 | 2100 MPa | 10 Kj/m2 | HB | |
| Isoryl® A 20 90 GF20 W | PPO 20% glass fiber, WRAS approved. | 1,21 g/cm3 | 4500 MPa | 3 Kj/m2 | HB | |
| Isoryl® A 20 10 GF30 W | PPO 30% glass fiber, WRAS approved. | 1,27 g/cm3 | 6000 MPa | 3 Kj/m2 | HB | |
| Isoryl® A 20 75 GF20 V0 | PPO 20% glass fiber, flame retardant UL94 V0 3,00mm. | 1,24 g/cm3 | 4500 MPa | 3 Kj/m2 | V0 | |
| Isoryl® A 120 T20 V1 A | PPO 20% mineral filled, flame retartant UL94 V1 1,5mm. | 1,21 g/cm3 | 3600 MPa | 5 Kj/m2 | V1 YC | |
| Isoryl® A 120 GF0 V0 | PPO flame retardant UL94 V0 1,5mm. | 1,10 g/cm3 | 2250 MPa | 9 Kj/m2 | V0 YC |
Isonyl®
Compounds based on polyamide 6 and 66 (PA6 – PA66), with good heat resistance and good mechanical properties. Our portfolio includes different grades, reinforced with glass and carbon fiber or mineral filled; impact modified, lubricated with Silicon, PTFE or Molybdenum disulfide; halogen or halogen-free flame retardant base, UL94 listed. Our products can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isonyl® A 6 | PA6 general purpose for injection moulding. | 1,13 g/cm3 | 2700 MPa | 4 Kj/m2 | V2 | |
| Isonyl® A 6 ST | PA6 impact modified. | 1,13 g/cm3 | 2400 MPa | 8 Kj/m2 | HB | |
| Isonyl® A 6 ST1 | PA6 impact modified. | 1,12 g/cm3 | 2300 MPa | 20 Kj/m2 | HB | |
| Isonyl® A 6 ST2 | PA6 impact modified. | 1,11 g/cm3 | 2000 MPa | 30 Kj/m2 | HB | |
| Isonyl® A 6 STZ | PA6 impact modified. | 1,10 g/cm3 | 1800 MPa | 40 Kj/m2 | HB | |
| Isonyl® A 6 STZX | PA6 high impact modified. | 1,08 g/cm3 | 1600 MPa | 70 Kj/m2 | HB | |
| Isonyl® A 6 GF15 | PA6 15% glass fiber reinforced. | 1,21 g/cm3 | 6000 MPa | 7 Kj/m2 | HB | |
| Isonyl® A 6 GF50 | PA6 50% glass fiber reinforced. | 1,56 g/cm3 | 12000 MPa | 13 Kj/m2 | HB | |
| Isonyl® A 6 GF60 | PA6 60% glass fiber reinforced. | 1,70 g/cm3 | 19000 MPa | 16 Kj/m2 | HB | |
| Isonyl® A 6 GS30 | PA6 30% glass beads reinforced. | 1,34 - 1,36 g/cm3 | 3150 MPa | 3 Kj/m2 | HB | |
| Isonyl® 6 GF30 V0 HF | PA6 30% glass fiber, flame retardant UL94 V0 1,5 mm, halogen free. | 1,41 g/cm3 | 9000 MPa | 6 Kj/m2 | V0 YC | |
| Isonyl® A 66 | PA66 general purpose for injection moulding. | 1,14 g/cm3 | 2900 MPa | 4 Kj/m2 | V2 | |
| Isonyl® A 66 ST | PA66 impact modified. | 1,13 g/cm3 | 2500 MPa | 9 Kj/m2 | HB | |
| Isonyl® A 66 ST1 | PA66 impact modified. | 1,12 g/cm3 | 2400 MPa | 20 Kj/m2 | HB | |
| Isonyl® A 66 ST2 | PA66 impact modified. | 1,11 g/cm3 | 2200 MPa | 30 Kj/m2 | HB | |
| Isonyl® A 66 STZ | PA66 impact modified. | 1,10 g/cm3 | 2000 MPa | 40 Kj/m2 | HB | |
| Isonyl® A 66 STZX | PA66 high impact modified. | 1,08 g/cm3 | 1800 MPa | 65 Kj/m2 | HB | |
| Isonyl® A 66 GF30 | PA66 30% glass fiber reinforced. | 1,36 g/cm3 | 8500 MPa | 12 Kj/m2 | HB | |
| Isonyl® A 66 GF50 | PA66 50% glass fiber reinforced. | 1,56 g/cm3 | 14000 MPa | 13 Kj/m2 | HB | |
| Isonyl® A 66 GF25 V0 | PA66 25% glass fiber, flame retardant UL94 V0 1,5 mm, with halogens. | 1,50/1,55 g/cm3 | 8500 MPa | 9 Kj/m2 | V0 | |
| Isonyl® A 6 GF30 | PA 6 30% glass fiber reinforced. | 1,36 g/cm3 | 8000 Mpa | 12 Kj/m2 | HB | |
| Isonyl® A 6 GF30 ST2 | PA6 30% glass fiber reinforced, impact modified. | 1,32 g/cm3 | 6800 Mpa | 17 Kj/m2 | HB | |
| Isonyl® A 6 GF30 HSR | PA6 30% glass fiber reincorced, good impact resistance, heat and hydrolysis resistant. | 1,36 g/cm3 | 8000 Mpa | 12 Kj/m2 | HB | |
| Isonyl® A 6 GF35 | PA6 35% glass fiber reinforced. | 1,38 - 1,41 g/cm3 | 9000 Mpa | 15 KJ/m2 | HB | |
| Isonyl® A 6 GF30 ST | PA6 30% glass fiber reinforced, impact modified. | 1,34 g/cm3 | 7300 Mpa | 14 KJ/m2 | HB |
Green Isonyl®
Polyamide 6 with Glass Fiber reinforcement formulated with partial use of post-industrial compound and recycled feedstocks. The products are available in accordance with some standards recently introduced by the automotive and tools sectors in black colors.| Name | Compound | Density ISO 1183 | MEF ISO 178 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Green Isonyl® I 66 GF25 GW | 25% glass fiber reinforced polyamide 66. Flame retardant grade with GWFI 850°C on 2 mm thickness. Recycled content. | / | 7500 MPa | 7 KJ/m2 | / |
Isoter®
Styrenic Compound (ABS-SAN-ASA) available in different grades in a wide range of melt flow rates, impact and heat resistance, in accordance with market demands and industry standards. Some products are available glass fiber reinforced; HB class and halogen-based flame retardant with UL94 certification. They can be tailor made colored, upon specific customer requirements, with high or low gloss.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoter® A 20 180 | ABS medium flow, general purposes, good impact resistance. | 1,04 g/cm3 | 20 gr/10' | 17 Kj/m2 | HB | |
| Isoter® A 35 200 | ABS high flow, general purpose, good impact resistance. | 1,04 g/cm3 | 35 gr/10' | 16 Kj/m2 | HB | |
| Isoter® A 15 250 AS | ABS medium flow, improved chemical resistance. | 1,04 g/cm3 | 20 gr/10' | 24 Kj/m2 | HB | |
| Isoter® A 10 120 HT | ABS with high heat resistance Vicat B/50 102°C | 1,05 g/cm3 | 10 gr/10' | 12 Kj/m2 | HB | |
| Isoter® A 10 150 HT | ABS with high heat resistance Vicat B/50 105°C. | 1,05 g/cm3 | 10 gr/10' | 12 Kj/m2 | HB | |
| Isoter® A 5 150 HT LE | ABS very high heat resistance Vicat B/50 108°C, low emission. | 1,05 g/cm3 | 6 gr/10' | 18 Kj/m2 | HB | |
| Isoter® A 30 200 FR V0 | ABS flame retardant, UL94 V0 1,5mm. | 1,20 g/cm3 | 30 gr/10' | 20 Kj/m2 | V0 YC | |
| Isoter® A 10 100 GF17 | ABS 17% glass fiber reinforced. | 1,18 g/cm3 | 10 gr/10' | 6 Kj/m2 | HB |
Isoclear®
Polycarbonate Compounds (PC) offering a good combination of toughness, impact strength and high heat resistance. Our products can be glass fiber reinforced and impact modified. They are UL94 certified for flame retardance, available both halogenated and halogen-free base. They can be colored upon specific customer requirements, also in transparent colors.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isoclear® A 20 60 | PC low viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,2 g/cm3 | 20 gr/10' | 60 Kj/m2 | HB | |
| Isoclear® A 10 60 | PC medium viscosity, good mechanical and high heat resistance, for transparent and solid colors. | 1,2 g/cm3 | 10 gr/10' | 60 Kj/m2 | HB | |
| Isoclear® A 10 60 GF0 V0 | PC flame retardant, with halogens, UL94 V0 1,6 mm. | 1,20 g/cm3 | 10 gr/10' | 50 Kj/m2 | V0 YC | |
| Isoclear® A 10 60 GF10 V0 | PC 10% glass fiber reinforced, flame retardant, with halogens, UL94 V0 1,6 mm. | 1,26 - 1,30 g/cm3 | 10 gr/10' | 7 Kj/m2 | V0 YC |
Isostyr®
Styrenic Compound (PS) available in different grades, impact and heat resistance in accordance with the industry standards of household appliances and electric market. Some products are available halogen-based flame retardant. They can be tailor made colored, upon specific customer requirements.| Name | Compound | Density ISO 1183 | MFI ISO 1133 | Izod Notched ISO 180/1A | Flammability UL94 | |
|---|---|---|---|---|---|---|
| Isostyr® A 10 50 | HIPS medium impact, good heat resistance and high stiffness. | 1,04 g/cm3 | 10 gr/10' | 5 Kj/m2 | HB | |
| Isostyr® A 10 100 V2 | HIPS flame retardant UL94 V2 1,5 mm. | 1,13 g/cm3 | 20 gr/10' | 7 Kj/m2 | V2 |